Adsorption of cis-1,4-polyisoprene at solid/liquid interface

The adsorption of cis‐1,4‐polyisoprene on alumina and silica gel was studied at three temperatures. The solvents used were toluene, chlorobenzene and various mixtures of both. The adsorption from the mixtures of the solvents was much less than from either of the pure solvents. The amount of adsorpti...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Die Angewandte makromolekulare Chemie 1994-03, Vol.220 (1), p.21-37
Hauptverfasser: Vangani, Veena, Rakshit, Animesh Kumar
Format: Artikel
Sprache:eng
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:The adsorption of cis‐1,4‐polyisoprene on alumina and silica gel was studied at three temperatures. The solvents used were toluene, chlorobenzene and various mixtures of both. The adsorption from the mixtures of the solvents was much less than from either of the pure solvents. The amount of adsorption was an inverse function of temperature. The thermodynamic quantities of adsorption at infinite dilution were obtained by extrapolation and at isosteric conditions. They were computed and discussed for all the systems. Die Adsorption von Poly(cis‐1,4‐isopren) an Aluminiumoxid‐ und Siliziumdioxid‐Oberflächen wurde bei verschiedenen Temperaturen untersucht. Die Adsorptionsausbeute verhielt sich umgekehrt proportional zur Temperatur und war aus Toluol‐ und Chlorbenzol‐Lösungen größer als aus Mischungen von Toluol und Chlorbenzol. Die thermodynamischen Adsorptionsparameter bei unendlicher Verdünnung und isosteren Bedingungen wurden durch Extrapolation ermittelt und für alle untersuchten Systeme diskutiert.
ISSN:0003-3146
1522-9505
DOI:10.1002/apmc.1994.052200103