Effects of processing variables on the mechanical properties of compression molded polystyrene-wood fiber composites

Optimization of mixing and molding conditions (e.g. temperature, time and pressure) of aspen chemithermomechanical pulp (CTMP)‐polystyrene composites was carried out. Compounding conditions showed a substantial effect on the mechanical properties of the composites. The effect of fiber encapsulation with polystyrene on the mechanical properties of the composites was also evaluated. Compared to non‐encapsulated ones, the mechanical properties of composites showed superior results when encapsulated CTMP fibers were used. After encapsulation of wood fibers, and optimization of mixing and molding conditions, composites with up to 36% of fiber volume fraction could be incorporated in polystyrene with improved mechanical properties. Die Misch‐ und Spritzgießbedingungen (Temperatur, Zeit und Druck) für die Verarbeitung von mit chemithermomechanischem Espenzellstoff (CTMP) verstärktem Polystyrol wurden optimiert. Die Verarbeitungsbedingungen wirkten sich wesentlich auf die mechanischen Eigenschaften des Verbundmaterials aus. Außerdem wurde der Einflußeiner zusätzlichen Faserverkapselung mit Polystyrol auf die mechanischen Eigenschaften untersucht, die im Vergleich zu den Verbunden ohne Faserverkapselung bessere Werte ergaben. Mit dem verkapselten CTMP konnte eine Verbesserung der mechanischen Eigenschaften bei einem Fasergehalt von bis zu 36 Vol.‐% erreicht werden.