Solution properties of ultrahigh molecular weight polymers, 15. A viscometric study of poly(isobutyl methacrylate) in different solvents

The paper extends previous studies on ultrahigh molecular weight synthetic polymers. The intrinsic viscosities and the viscosity constants of poly(isobutyl methacrylate) fractions were obtained by the methods of Huggins, Kraemer, Martin, Schulz‐Blaschke, and Fedors in CCl4 and C6H6 at 25°C. It was observed that the method of Fedors is not very sensitive to the possible errors appearing in estimating the relative viscosities in higher concentration domains. This method yields intrinsic viscosity values close to the mean values obtained from the other five methods and to the values calculated according to the averaging procedure suggested by Sakai. The transition concentrations separating the concentration domains (diluted‐semidiluted) and the Mark‐Houwink constants were obtained. Die Arbeit stellt eine Erweiterung der vorhergehenden Untersuchungen hinsichtlich synthetischer Polymerer mit sehr großen Molekularmassen dar. Die Grenzviskositäten und die Viskositätskonstanten von Poly(isobutylmethacrylat) wurden mit den Methoden von Huggins, Kraemer, Martin, Schulz‐Blaschke und Fedors in CCl4 und C6H6 bei 25°C erhalten. Es wurde beobachtet, daß die Methode von Fedors nicht sehr sensibel ist bei den möglichen Fehlern, die bei der Bestimmung der relativen Viskositäten in konzentrierten Bereichen auftreten. Diese Methode führt zu Grenzviskositäten, die nahe den mittleren Werten liegen, die mit den anderen fünf Methoden und der Sakai‐Mitteilung erhalten wurden. Außerdem wurden die Umwandlungskonzentrationen, die die verdünnt‐halbverdünnten Bereiche trennen, sowie die Mark‐Houwink‐Konstanten bestimmt.