Interface distribution functions of isotactic polystyrene - poly(2,6-dimethylphenylene oxide) blends

Morphological parameters of isotactic polystyrene (iPS) · poly(2,6‐dimethylphenylene oxide) (PPO) blends have been determined from measurements of the small angle X‐ray scattering by calculating interface distribution functions. Applied to the compatible system iPS/PPO this method yields a number of reliable parameters such as the long period and mean thicknesses of crystal lamellae and interlamellar spacings. A comparison of the results obtained from the calculation of the interface distribution functions with those derived from model calculations show that theoretical calculations using the density model yield essentially the same results. Aus der Röntgenkleinwinkelstreuung an Legierungen von isotaktischem Polystyrol (iPS) und Poly(2,6‐dimethylphenylenoxid) (PPO) wurden Strukturparameter durch Berechnung von Grenzflächenverteilungsfunktionen bestimmt. Es konnte gezeigt werden, daß eine Reihe von Parametern wie die mittlere Dicke von Lamellen und interlamellaren Abständen sowie die Langperiode trotz z. T. großer Unsicherheiten bei der Korrektur der experimentellen Streukurve mit großer Genauigkeit bestimmt werden können. Die aus Grenzflächenverteilungsfunktionen bestimmten Werte wurden mit Ergebnissen aus Modellstreukurvenberechnungen verglichen. Dabei stellte sich heraus, daß theoretische Berechnungen mit einem Modell, das zusätzlich zur kristallinen und amorphen Dichte die mittlere Dichte der Probe berücksichtigt, im wesentlichen dieselben Parameter liefern wie die aus den Grenzflächenverteilungsfunktionen bestimmten.