Styrene-divinylbenzene copolymers, IV. Structure and texture changes during synthesis

Styrene‐divinylbenzene macroporous resins were prepared with the same composition (13% DVB), but varying diluent amount of benzyl alcohol. From sample analysis, the copolymerization kinetics concerning both monomer consumption and residual double bond amount were determined. Porous texture and morphology analyses by BET Brunauer, Emmett, Teller. , BJH E. P. Barrett, L. G. Joyner, P. P. Halenda, J. Am. Chem. Soc. 73 (1951) 373. , Mercury porosimetry, and scanning electron microscopy were carried out, too. Depending on diluent amount, the final product is classified as inside or outside the macroporous domain. Texture evolution is clearly different for the two classes of products, although their chemical evolutions are almost the same. A qualitative discussion of porous texture formation is presented, based on occurrence of three critical events: gelation, phase separation and molecular overlap. Es wurden makroporöse Styrol‐Divinylbenzol‐Harze bei gleicher Zusammensetzung (13% Divinylbenzol), aber mit variierenden Verdünnunganteilen von Benzylalkohol, hergestellt. Aus der Analyse der Proben wurde die Copolymerisationskinetik sowohl aufgrund des Monomerverbrauchs als auch des Doppelbindungsanteils bestimmt. Ebenso wurden Porenstruktur‐ und Morphologieanalysen mittels BET, BJH, Quecksilberporosimetrie und Rasterelektronenmikroskopie durchgeführt. In Abhängigkeit vom Anteil an Verdünnungsmittel wurde das Endprodukt als innerer oder äußerer makroporöser Bereich klassifiziert. Die Strukturbildung ist für die zwei Produktklassen unterschiedlich, obwohl ihre chemische Entstehung nahezu gleich ist. Es wird eine qualitative Diskussion über die Bildung der lockeren Struktur gegeben, die auf drei kritischen Erscheinungen beruht: Gelbildung, Phasentrennung und molekulare Überlappung.