Studies on syntheses and permeabilities of special polymer membranes, 32. New preparation method of cellulose membranes
The preparation of cellulose membranes from mixtures of cellulose, nonprotonic polar organic solvents, paraformaldehyde, and basic catalyst was studied. When dimethyl sulfoxide was used as casting solvent, the resulting membrane was the densest. An increase of an additional amount of triethyl amine...
Gespeichert in:
Veröffentlicht in: | Die Angewandte makromolekulare Chemie 1982-01, Vol.102 (1), p.9-16 |
---|---|
Hauptverfasser: | , , |
Format: | Artikel |
Sprache: | eng |
Online-Zugang: | Volltext |
Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
Zusammenfassung: | The preparation of cellulose membranes from mixtures of cellulose, nonprotonic polar organic solvents, paraformaldehyde, and basic catalyst was studied. When dimethyl sulfoxide was used as casting solvent, the resulting membrane was the densest. An increase of an additional amount of triethyl amine used as basic catalyst gave denser membranes.
Es wurde die Herstellung von Cellulosemembranen aus Celluloselösungen in einem Gemisch von Paraformaldehyd, nicht protonischem, polarem, organischem Lösungsmittel und einem basischen Katalysator untersucht. Die dichtesten Membranen wurden mit Dimethylsulfoxid als Lösungsmittel erhalten, wobei die Dichte der Membranen bei einem Zusatz von Triethylamin zunahm. |
---|---|