Studies on syntheses and permeabilities of special polymer membranes. XI. Permeation characteristics of grafted poly(vinyl alcohol) membranes

The permeation characteristics of membranes grafted with various vinyl monomers onto poly(vinyl alcohol) were investigated by changing the mixture in graft copolymerization, the heat treatment and feed temperature. It was found that changes in permeation characteristics relate to changes of physical structure, such as micro‐phase separation and compaction under pressure, and of chemical structure, such as fraction of hydrophilic and hydrophobic groups in the resulting membranes. By comparing the permeation charactersitics for several feed solutes of the grafted membranes (methylmethacrylate grafted onto poly(vinyl alcohol) and onto poly(ethylene glycol)), it was found that the interaction between feed solute molecules and membrane substrate is an important factor. Das Permeationsverhalten von Membranen aus mit verschiedenen Vinylmonomeren gepfropftem Polyvinylalkohol wurde auf Veränderungen in den Bedingungen der Pfropfreaktion, der Warmbehandlungstemperaturen und der Permeationstemperaturen untersucht. Das Permeationsverhalten ändert sich mit Veränderungen der physikalischen und der chemischen Struktur der erhaltenen Membranen. Aus dem Vergleich des Permeationsverhaltens für verschiedene gelöste Stoffe von Membranen aus Polyvinylalkohol, gepfropft mit Methylmethacrylat und Polyäthylenglykol, gepfropft mit Methylmethacrylat, ergab sich, daß Wechselwirkungen zwischen den Molekülen des gelösten Stoffs und der Membran ein wichtiger Faktor sind.