Poly(2,4‐perfluoroalkylene‐6‐Perfluoroalkyltriazine)s, new high temperature elastomers

Poly(perfluoroalkyleneimidoylperfluoroalkylenoamidine)s have been prepared by the reaction of perfluoroalkane dinitriles with ammonia or with the diamidines of the dinitriles. The imidoylamidine polymers were treated with anhydrides to give poly(perfluoroalkyIenetriazine)s. Treatment of the imidoylamidine polymer with perfluoroglutaric anhydride or 4‐cyanoperfluorobutyryl chloride gave pendant carboxyl or nitrile groups, respectively, on the triazine polymer which served as crosslinking sites. The formation of triazine crosslinks from the nitrile‐pendant groups by trimerization with catalysts such as tetraphenyltin has given crosslinked polymers with tensile strengths of 1500 p.s.i., 70% elongation, and with thermal stability aproaching that of the original gum. The milling of catalysts and fillers with the polymer decreased the thermal stability in comparison with the original gum. PolyperfluoralkyIenimidoyl‐perfluoralkylenamidine wurden durch Reaktion von Perfluoralkandinitrilen mit Ammoniak oder mit den Diamidinen der Nitrile hergestellt. Die Imidoylamidin‐Polymeren wurden mit Anhydriden zu Polyperflouralkylentriazinen umagesetzt. Mit Perfluorglutarsäureanhydrid oder 4‐Cyanoperfluorbutyrylchlorid entstanden Triazine mit anhängenden Carboxyl‐ bzw. Nitrilgruppen, die als Vernetzungsstellen dienten. Bei der Vernetzung durch Trimerisation mit Katalvsatoren wie Tetraphenylzinn ergaben sich vernetzte Polymere mit Zugfestigkeiten von 1500 p.s.i., 70% Dehnung, und hoher thermischer Stabilität. Beim Vermahlen von Katalysatoren und Füllstoffen mit dem Polymeren nahm die Temperaturbeständigkeit gegenüber der Ausgangsprobe ab.