Black Liquor and Wood Char-Derived Nitrogen-Doped Carbon Materials for Supercapacitors

Herein, we present a synthesis route for high-efficiency nitrogen-doped carbon materials using kraft pulping residue, black liquor, and wood charcoal as carbon sources. The synthesized nitrogen-doped carbon materials, based on black liquor and its mixture with wood charcoal, exhibited high specific...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Hauptverfasser: Tamasauskaite-Tamasiunaite, Loreta, Jablonskienė, Jolita, Šimkūnaitė, Dijana, Volperts, Aleksandrs, Plavniece, Ance, Dobele, Galina, Zhurinsh, Aivars, Jasulaitiene, Vitalija, Niaura, Gediminas, Drabavicius, Audrius, Juel, Mari, Rausseo, Luis César Colmenares, Kruusenberg, Ivar, Kaare, Kätlin, Norkus, Eugenijus
Format: Artikel
Sprache:eng
Online-Zugang:Volltext bestellen
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:Herein, we present a synthesis route for high-efficiency nitrogen-doped carbon materials using kraft pulping residue, black liquor, and wood charcoal as carbon sources. The synthesized nitrogen-doped carbon materials, based on black liquor and its mixture with wood charcoal, exhibited high specific surface areas (SSAs) of 2481 and 2690 m2 g−1, respectively, as well as a high volume of mesopores with an average size of 2.9–4.6 nm. The nitrogen content was approximately 3–4 at% in the synthesized nitrogen-doped carbon materials. A specific capacitance of approximately 81–142 F g−1 was achieved in a 1 M Na2SO4 aqueous solution at a current density of 0.2 A g−1. In addition, the specific capacitance retention was 99% after 1000 cycles, indicating good electrochemical stability.