铝含量对Pd–S2O82-/ZrO2–Al2O3固体超强酸催化剂的异构化性能的影响（英文）

The effect of Al content on the performance of the Pd–S2O82-/Zr O2–Al2O3solid superacid catalyst was studied using n-pentane isomerization as a probe reaction. The catalysts were also characterized by X-ray diffraction(XRD), Fourier transform Infrared(FTIR), specific surface area measurements(BET), thermogravimetry–differential thermal analysis(TG–DTA), H2-temperature programmed reduction(TPR) and NH3temperature-programmed desorption(NH3-TPD). The Pd–S2O82-/Zr O2–Al2O3catalyst made from Al2O3 mass fraction of 2.5% exhibited the best performance and its catalytic activity increased by 44.0% compared with Pd–S2O82-/Zr O2. The isopentane yield reached64.3% at a temperature of 238 °C, a reaction pressure of 2.0 MPa, a space velocity of 1.0 h-1and a H2/n-pentane molar ratio of 4.0. No obvious catalyst deactivation was observed within 100 h.