Hot corrosion behavior of the spray-formed nickel-based superalloy简

An investigation of low temperature hot corrosion is carried out on a spray-formed nickel-based superalloy FGH100pre-coated with Na2SO4- NaCl at 700℃ for 100 h. Mass gain measurement, x-ray diffraction, scanning electron microscopy, and energy dispersive x-ray spectroscopy are used to study the corrosion behavior. Results reveal that corrosion behavior follows a sequence, that is, first rapidly proceeding, then gradually slowing down, and finally forming an outer layer composed of different types of oxides and an inner layer mainly comprised of sulfides. In-depth analysis reveals that the hot corrosion of FGH100 is a combined effect of oxidation-sulfidation and transfer of oxides.