Effect of Diatomite Additive on the Meehanieal and Dieleetrie Properties of Porous SiO2-Si3N4 Composite Ceramics
Porous SiO2-Si3N4 composite ceramics with high porosity and excellent mechanical properties were fabricated by pressureless-sintering at relatively low temperature of 1 500 ~C using diatomite as pore forming agent. The effects of diatomite on flexural strength, fracture toughness, shrinkage, porosit...
Gespeichert in:
Veröffentlicht in: | 武汉理工大学学报:材料科学英文版 2016 (3), p.528-532 |
---|---|
1. Verfasser: | |
Format: | Artikel |
Sprache: | eng |
Schlagworte: | |
Online-Zugang: | Volltext |
Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
Zusammenfassung: | Porous SiO2-Si3N4 composite ceramics with high porosity and excellent mechanical properties were fabricated by pressureless-sintering at relatively low temperature of 1 500 ~C using diatomite as pore forming agent. The effects of diatomite on flexural strength, fracture toughness, shrinkage, porosity and phase transformation of the porous ceramics were investigated in detail. Compared with that of the ceramic without adding diatomite, the porosity of the ceramic with 10% diatomite is increased by about 27.4%, the flexural strength and fracture toughness reaches 78.04 MPa and 1.25 MPa.m1/2, respectively. As the porosity increases, the dielectric constant of porous SiO2-Si3N4 ceramic decreases obviously from 3.65 to 2.95. |
---|---|
ISSN: | 1000-2413 1993-0437 |