Up-conversion luminescence properties and energy transfer of Er^3＋/Yb^3＋ co-doped oxyfluoride glass ceramic containing CaF2 nano-crystals

The Er^3＋/yb^3＋ co-doped transparent oxyfluoride glass-ceramics containing CaF2 nano-crystals were successfully prepared. After heat treatments, transmission electron microscopy （TEM） images showed that CaF2 nano-crystals of 20-30 nm in diameter precipitated uniformly in the glass matrix. luminescence of Er^3＋ at 540 nm and 658 nm was observed in Comparing with the host glass, high efficiency upconversion the glass ceramics under the excitation of 980 nm. Moreover, the size of the precipitated nano-crystals can be controlled by heat-treatment temperature and time. With the increase of the nano-crystal size, the intensity of the red emission increased more rapidly than that of the green emission. The energy transfer process of Er^3＋ and Yb^3＋ was convinced and the possible mechanism of Er^3＋ up-conversion was discussed.