Effect of Magnesia Blending on the Magnetic Properties of Grain Oriented Silicon Steel

Decarburized samples of grain oriented silicon steel were coated with alone and blended magnesias and submitted to the high temperature annealing. The magnesias and their blendings were characterized using granulometry measurements, ignition loss and reactivity tests. After high temperature annealing, forsterite film morphology, magnetic properties and Goss deviation were also analyzed. Better magnetic properties and sharper Goss orientation were found in samples which had used blended magnesias. These results are explained by the magnesias particle size distributions, forsterite film formation and rate of inhibitors release.