Refinement of primary Si in Cu-50Si alloys with novel AI-Zr-P master alloy

In this article, a novel Al-6Zr-2P master alloy with ZrP particles was successfully synthesized, and the refining performance of this novel master alloy for the primary Si in Cu-50Si alloys was also investigated. By means of the fracture plane observation, it is found that the ZrP phase would precipitate first in the solidification pro- cess, and then, the ZrAl3 phase grows around them. Fur- thermore, it is observed that the refining effect can be remarkably improved by changing the addition sequence of the raw materials. After the melting of commercial Cu, the 2.0 wt% Al-6Zr-2P master alloy and crystalline Si were added in sequence, and the mean size of the primary Si in Cu-50Si alloy can be significantly refined from 255.7 to 75.3 gm. Meanwhile, the refining mechanism was dis- cussed in detail.