Microstructure and Mechanical Properties of Poly （Vinyl Chloride） Modified by Silica Fume /Acrylic Core-Shell Impact Modifier Blends

This research explored replacing acrylic core-shell impact modifier （AIM） by silica fume to toughen PVC. 100%, 75%, 50% and 25% of AIM （8 phr） were substituted by silica fume in PVC respectively, and then processed by dry blending and twin-screw extrusion. Severe silica fume agglomeration was observed by scanning electron microscope （SEM） in the PVC matrix when 8 phr pure silica fume was used and processed by screw speed of 20 rpm. Its tensile strength was thereby reduced by 38% comparing to unmodified PVC. The silica fume was successfully dispersed while the screw speed was slowed down to 10 rpm to give a stronger screw torque and a longer melt residential time in the extruder. The tensile strength was ’recovered’ to a level comparable to unmodified PVC. Impact test were performed on all formulations extruded at 10 rpm screw speed and synergetic toughening effect was found with 50% substitution and it had the impact strength that was comparable to 8 phr pure AIM toughened PVC.