Change in the Pore Structure of Carbon-Carbon Composites during Successive Stages of High-Pressure Impregnation and Heat Treatment

Pore structure of C/C （Carbon-Carbon） composite after several stages of pitch impregnation under the high pressure and heat treatment was investigated by means of low temperature nitrogen adsorption and the standard contact porosimetry. Total pore volume, pore size distribution and specific surface area were calculated for samples of composite after several successive stages of treatment. The radius of pores presented in the material changes from 1 nm to 90 tam. Total pore volume and specific surface area both decrease after successive stages of pitch impregnation under the pressure, whereas heat treatment up to 1,750 ℃ and 2,000 ℃ leads to creation of some porous space and pore volume expansion. The bulk porosity of C/C composite comes down from 33.7% to 13.7% after the serial stages of treatment and the specific surface area is reduced by half compared to the initial material.