High-Temperature Oxidation Resistance of Austenitic Stainless Steel Crl8Nil 1Cu3Al3MnNb

The kinetic curve of the high-temperature oxidation of austenitie stainless steel Crl8Ni11 Cu3Al3MnNb at different temperatures was measured by weighting method. It is showed that the oxidation curves at 700 and 800 ℃ followed the parabolic law, and the steel presented an excellent anti-oxidation. The surface morphology and structure of the oxide film were studied by scanning electron microscopy and X-ray diffraction methods. A dense oxide film was attained at 700 and 800 ℃, mainly composed of the hexagonal Al2 O3, Fe2 O3, and a small amount oxide of Cr at 700 ℃. At 900 ℃ the oxide film started to delaminate, and was composed of （Cr,Fe）2O3 and the spinel CuCrMnO4 and Fe（Cr, Al） 2O3.