Photovoltaic characteristics of Ca3Co409/Nb-doped SrTiO3 heterojunction
Ca3Co409/Nb-SrTiO3 heterojunction with good rectifying behavior at room temperature was fabricated by growing a layer of Ca3Co409 film on the lwt% Nb-doped SrTiO3 substrate by means of the chemical solution deposition technique. A large open-circuit voltage signal with the response time of tens of n...
Gespeichert in:
Veröffentlicht in: | 中国科学:物理学、力学、天文学英文版 2012, Vol.55 (5), p.772-775 |
---|---|
1. Verfasser: | |
Format: | Artikel |
Sprache: | eng |
Schlagworte: | |
Online-Zugang: | Volltext |
Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
Zusammenfassung: | Ca3Co409/Nb-SrTiO3 heterojunction with good rectifying behavior at room temperature was fabricated by growing a layer of Ca3Co409 film on the lwt% Nb-doped SrTiO3 substrate by means of the chemical solution deposition technique. A large open-circuit voltage signal with the response time of tens of nanosecond was observed at room temperature when the Ca3Co409 layer of the heterojunction was illuminated under the 308 nm irradiation and no voltage signal was detected under the 10.6 gun irradiation. A mechanism based on the photovoltaic effect of a p-n junction was proposed to explain the experimental results. The present work shows a great potential of this new heterojunction as photoelectric devices. |
---|---|
ISSN: | 1674-7348 1869-1927 |