Microstructure,tensile and creep properties of as-cast Mg-3.8Zn-2.2C（a-x）Ce（x=0,0.5,1 and 2 wt.%） magnesium alloys

The microstructure and mechanical properties of as-cast Mg-3.8Zn-2.2Ca alloy with different Ce contents were investigated by both optical and electron microscopy, X-ray diffraction, differential scanning calorimetry analysis, tensile and creep tests. The results indi-cated that adding 0.41 wt.%-1.83 wt.% Ce could refine the grains of the alloy, and the grain size gradually decreased as the Ce content in-creased. Furthermore, addition of either 0.41 wt.% or 0.89 wt.% Ce caused the morphology of the Ca2Mg6Zn3 phase to change partially from semi-continuous block to discrete fine particles. However, after adding 1.83 wt.% Ce, portions of the Ca2Mg6Zn3 and Mg12Ce phases were mixed and this Ca2Mg6Zn3＋Mg12Ce eutectic changed to a different coarse semi-continuous morphology. In addition, addition of 0.41 wt.%-1.83 wt.% Ce improved the tensile and creep properties of the alloy. Amongst these Ce-containing alloys, the alloy with 0.89 wt.% Ce exhibited the best ultimate tensile strength and elongation while the alloy with 1.83 wt.% Ce had the best yield strength and creep properties.