The magnetization reversal behaviour for SmCo6.8Zr0.2 and SmCo6.8Zr0.2a-（Fe,Co） nanocrystalline magnets at low temperature

This paper reports that the SmCo6.8Zr0.2 nanocrystalline permanent magnets and SmCo6.8Zr0.2/a-（Fe,Co） nanocomposite permanent magnets are successfully produced by mechanical alloying and subsequently annealing at 700℃ for 10 minutes. The x-ray diffraction results show that the phase structure of SmCo6.8Zr0.2 nanocrystalline permanent magnets is composed of SmCo7 phase and SmCo6.8Zr0.2/a-（Fe,Co） nanocomposite permanent magnets is composed of SmCo7 and a-（Fe,Co） phases. The mechanism of magnetization reversal is mainly controlled by inhomogeneous domain wall pinning in SmCo6.8Zr0.2 and SmCo6.8Zr0.2/a-（Fe,Co） magnets. The inter-grain exchange interaction at low temperature is investigated, which shows that the inter-grain exchange interaction of SmCo6.8Zr0.2/a-（Fe,Co） magnets increases greatly by the decrease of the measured temperature. According to Amirr-H/Hcj, Amrev-H/Hcj and Xirr-H/Hcj curves at room temperature and 100 K, the changes of irreversible and reversible magnetization behaviours of SmCo6.8Zr0.2 and SmCo6.8Zr0.2/a-（Fe,Co） magnets with the decreasing temperature are analysed in detail. The magnetic viscosity and the activation volume of SmCo6.8Zr0.2 and SmCo6.8Zr0.2/a-（Fe,Co） magnets at different temperatures are also studied.