MgO thickness-induced spin reorientation transition in Co0.9Fe0.1/MgO/Co0.9Fe0.1 structure

The magnetic anisotropy (MA) of Mo/Au/Co0.9Fe0.1/Au/MgO(0.7 - 3 nm)/Au/Co0.9Fe0.1/Au heterostructure has been investigated at room temperature as a function of MgO layer thickness (tMgO). Our studies show that while the MA of the top layer does not change its character upon variation of tMgO, the un...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:arXiv.org 2017-08
Hauptverfasser: Lasek, Kinga, Gladczuk, Leszek, Sawicki, Maciej, Aleshkevych, Pavlo, Przyslupski, Piotr
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:The magnetic anisotropy (MA) of Mo/Au/Co0.9Fe0.1/Au/MgO(0.7 - 3 nm)/Au/Co0.9Fe0.1/Au heterostructure has been investigated at room temperature as a function of MgO layer thickness (tMgO). Our studies show that while the MA of the top layer does not change its character upon variation of tMgO, the uniaxial out-of-plane MA of the bottom one undergoes a spin reorientation transition at tMgO of about 0.8 nm, switching to the regime where the coexistence of in- and out-of-plane magnetization alignments is observed. The magnitudes of the magnetic anisotropy constants have been determined from ferromagnetic resonance and dc-magnetometry measurements. The origin of MA evolution has been attributed to a presence of an interlayer exchange coupling (IEC) between Co0.9Fe0.1 layers through the thin MgO film.
ISSN:2331-8422
DOI:10.48550/arxiv.1708.07382