Surface Properties of Polymer Resins Fabricated with Subtractive and Additive Manufacturing Techniques

This study aimed to compare the surface roughness, hardness, and flexure strength of interim indirect resin restorations fabricated with CAD-CAM (CC), 3D printing (3D), and conventional techniques (CV). Twenty disk (3 mm x o10 mm) and ten bar specimens (25 x 2 x 2 mm) were fabricated for the CC, 3D, and CV groups, to be used for surface roughness, micro-hardness, and flexural strength testing using standardized protocol. Three indentations for Vickers micro-hardness (VHN) were performed on each disk and an average was identified for each specimen. Surface micro-roughness (Ra) was calculated in micrometers (mu m) using a 3D optical non-contact surface microscope. A three-point bending test with a universal testing machine was utilized for assessing flexural strength. The load was applied at a crosshead speed of 3 mm/min over a distance of 25 mm until fracture. Means and standard deviations were compared using ANOVA and post hoc Tukey-Kramer tests, and a p-value of 0.05). However, 3D showed significantly higher Ra compared to CC and CV samples (p < 0.05). Micro-hardness was significantly higher in 3D samples (p < 0.05) compared to CC and CV specimens. In addition, CC and CV showed comparable micro-hardness (p > 0.05). A significant difference in flexural strength was observed among the study groups (p < 0.05). CC and 3D showed comparable strength outcomes (p > 0.05), although CV specimens showed significantly lower (p < 0.05) strength compared to CC and 3D samples. The 3D-printed provisional restorative resins showed flexural strength and micro-hardness comparable to CAD-CAM fabricated specimens, and surface micro-roughness for printed specimens was considerably higher compared to CAD-CAM and conventional fabrication techniques.