Design of thermoset composites for high-speed additive manufacturing of lightweight sound absorbing micro-scaffolds
Low printing speeds in extrusion-based additive manufacturing of thermosets, such as direct ink writing, are an obstacle for industrial-scale production. This work aims at developing lightweight thermoset composite materials compatible with the high-speed direct ink writing of porous microstructures...
Gespeichert in:
Veröffentlicht in: | Additive manufacturing 2021-11, Vol.47, p.102245, Article 102245 |
---|---|
Hauptverfasser: | , , , , , , |
Format: | Artikel |
Sprache: | eng |
Schlagworte: | |
Online-Zugang: | Volltext |
Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
Zusammenfassung: | Low printing speeds in extrusion-based additive manufacturing of thermosets, such as direct ink writing, are an obstacle for industrial-scale production. This work aims at developing lightweight thermoset composite materials compatible with the high-speed direct ink writing of porous microstructures featuring a sound absorbing functionality. The developed materials are blends of an aerospace-grade epoxy matrix filled with different loadings of hollow glass microspheres and fumed silica nanoparticles. The printability of the blends was assessed through microscopy and tomography scans, by studying the shape retention for different filler loadings and nozzle configurations. Oscillatory, rotational, and capillary rheological studies were conducted to obtain viscosity models relating extrusion pressures and printing speeds. Three promising blends containing a combination of 0–10 wt% hollow glass microspheres and 0–12 wt% fumed silica were selected based on their printability and shape retention. Printing speeds ranging from 110 to 175 mm.s−1 were attained using 250 µm tapered nozzles, which is over three time the highest speeds reported in the literature. An acoustic absorption characterisation using a Kundt’s tube was carried out for printed porous microstructures resembling a log-pile network with 300 µm square pores. Average acoustic absorption coefficients above 0.6 were achieved for frequencies from 500 to 6000 Hz.
[Display omitted]
•3D printable epoxy systems contain hollow glass microspheres and/or fumed silica.•High fumed silica contents improve material elasticity and enable shape retention.•A modified empirical model predicts the flow behaviour of developed materials.•Printing speeds up to 175 mm/s pave the way for high-resolution large-area industrial production.•Efficient sound absorbing micro-scaffolds are printed using the developed composites. |
---|---|
ISSN: | 2214-8604 2214-7810 |
DOI: | 10.1016/j.addma.2021.102245 |