Effects of calcium addition on as-cast microstructure and mechanical properties of Mg-5Zn-5Sn alloy

The effects of Ca addition on the as-cast microstructure and mechanical properties of the Mg-5Zn-5Sn （mass fraction,%） alloy were investigated.The results indicate that an addition of 0.5%-1.5% （mass fraction） Ca to the Mg-5Zn-5Sn alloy not only refines the as-cast microstructure of the alloy but also causes the formation of the primary and/or eutectic CaMgSn phases with high thermal stability;an increase in Ca amount from 0.5% to 1.5% （mass fraction） increases the amount and size of the CaMgSn phase.In addition,Ca addition to the Mg-5Zn-5Sn alloy improves not only the tensile properties at room temperature and 150 ℃ but also the creep properties.Among the Ca-containing Mg-5Zn-5Sn alloys,the one added 0.5% （mass fraction） Ca obtains the optimum ultimate tensile strength and elongation at room temperature and 150 ℃,however,the alloy added 1.5% （mass fraction） Ca exhibits the optimum yield strength and creep properties.