Continuous dynamic recrystallization and discontinuous dynamic recrystallization in 99.99% polycrystalline aluminum during hot compression

The dynamic restoration behavior of 99.99% polycrystalline aluminum was investigated. The deformation was carried out by compression test at 533 - 773 K and initial strain rate of 0. 002 - 2 s^-1 to a true strain of 1.0 followed by water quench. Polarized optical microscopy and transmission electron...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Transactions of Nonferrous Metals Society of China 2005-02, Vol.15 (1), p.82-86
1. Verfasser: 刘楚明 蒋树农 张新明
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:The dynamic restoration behavior of 99.99% polycrystalline aluminum was investigated. The deformation was carried out by compression test at 533 - 773 K and initial strain rate of 0. 002 - 2 s^-1 to a true strain of 1.0 followed by water quench. Polarized optical microscopy and transmission electron microscopy were applied to observe the deformation microstructure. It's found that discontinuous dynamic recrystallization, which is commonly observed in lower stacking fault energy metals or ultra-high purity aluminum(≥99.999%), occurs when Zenner-Hollomon parameter(Z parameter) is low, but the true stress strain curve doesn't accompany stress oscillation.Continuous dynamic recrystallization occurs when Z parameter is intermediate, and only dynamic recovery takes place if Z parameter is high.
ISSN:1003-6326