VUV luminescence properties of Y0.95Eu0.05PO4 phosphor derived by a modified solid-state route

A modified solid-state route was attempted to prepare Y0.95 Eu0.05PO4 PDP phosphor, involving milling a powdered mixture of YCl3, EuCl3, and （NH4）2HPO4 and calcining the milling-derived precursor. The thermal decomposition behavior of the milling-derived precursor was investigated by thermogravimetric analysis （TGA）. Phase compositions, morphologies, and luminescence properties of the prepared phosphor powder were characterized by X-ray diffraction （XRD）, scanning electron microscope （SEM）, and vacuum ultraviolet （VUV） emission spectra, respectively. The results indicated that the Y0.95Eu0.05PO4 phosphor powder obtained at a calcination temperature of 900℃ was xenotime-structured. The phosphor powder particles were uniform and spherical-shaped with a primary particle size of-200 um. In comparison with that derived by the conventional solid-state route, the phosphor powder prepared by the modified solid-state route exhibited a higher color purity, presenting a predominant emission peak at 619 nm under 147 um VUV excitation.