Nanoscale precipitates and comprehensive strengthening mechanism in AISI H13 steel

The effects of heat treatment on the precipitates and strengthening mechanism in AISI H13 steel were investigated. The results showed that the presence of nanoscale precipitates favorably affected grain refinement and improved the yield strength. The volume fraction of precipitates increased from 1....

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:International journal of minerals, metallurgy and materials metallurgy and materials, 2016-09, Vol.23 (9), p.1056-1064
Hauptverfasser: Mao, Wen-wen, Ning, An-gang, Guo, Han-jie
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:The effects of heat treatment on the precipitates and strengthening mechanism in AISI H13 steel were investigated. The results showed that the presence of nanoscale precipitates favorably affected grain refinement and improved the yield strength. The volume fraction of precipitates increased from 1.05% to 2.85% during tempering, whereas the average precipitate size first decreased then increased during tempering. Contributions to the yield strength arising from the various mechanisms were calculated quantificationally, and the results demonstrated that grain refinement and dislocation density most strongly influenced the yield strength. In addition, under the interaction of average size and volume fraction, precipitates' contribution to the yield strength ranged from 247.9 to 378.5 MPa. Finally, a root-mean-square summation law of σ = σg + σs +(σd^2 + σp^2)^1/2, where σg, σs, σd, and σp represent the contributions of fine-grain strengthening, solid-solution strengthening, dislocation strengthening, and precipitation strengthening, respectively, was confirmed as the most applicable for AISI H13 steel, which indicates a strong link between precipitates and dislocations in AISI H13 steel.
ISSN:1674-4799
1869-103X
DOI:10.1007/s12613-016-1323-z