Effects of applied potential on the stress corrosion cracking behavior of 7003 aluminum alloy in acid and alkaline chloride solutions

Potentiodynamic polarization tests and slow strain rate test（SSRT） in combination with fracture morphology observations were conducted to investigate the stress corrosion cracking（SCC） behavior of 7003 aluminum alloy（AA7003） in acid and alkaline chloride solutions under various applied potentials（Ea...

Ausführliche Beschreibung

Gespeichert in:

Bibliographische Detailangaben
Veröffentlicht in:	International journal of minerals, metallurgy and materials metallurgy and materials, 2016-07, Vol.23 (7), p.819-826
Hauptverfasser:	Zhang, Xiao-yan, Song, Ren-guo, Sun, Bin, Lu, Hai, Wang, Chao
Format:	Artikel
Sprache:	eng
Schlagworte:	Aluminum Aluminum alloys Aluminum base alloys Anodic dissolution Ceramics Characterization and Evaluation of Materials Chemistry and Materials Science Chlorides Composites Corrosion Corrosion and Coatings Corrosion effects Corrosion potential Dissolution Glass Hydrogen embrittlement Hydrogen ion concentration Hydrogen ions Ion concentration Materials Science Metallic Materials Natural Materials Open circuit voltage SCC敏感性 Slow strain rate Stress corrosion Stress corrosion cracking Surfaces and Interfaces Thin Films Tribology 动电位极化应力腐蚀开裂开裂行为碱性溶液自密实混凝土酸性铝合金
Online-Zugang:	Volltext
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!

Schreiben Sie den ersten Kommentar!