Structural and impedance analysis of Ba0.9925Er0.0075TiO3 for microelectronic application

The Ba0.9925Er0.9975TiO3 ceramics that were prepared via solid-state reaction route were found to be phase pure at the final sintering temperature of 1350°C. The highest value of the dielectric constant is about 9000 measured at 10Hz and decreases to about 1000 at the Curie temperature at much highe...