Development of magnetorheological elastomers based on Deproteinised natural rubber as smart damping materials

Magnetorheological elastomers (MREs) are composite materials consist of micron-sized magnetizable particles carbonyl iron particles [CIPs]) embedded in a soft elastomer matrix. MRE technology offers variable stiffness and damping properties under the influence of a magnetic field. Herein, the feasibility of incorporating a new generation specialty rubber, Pureprena as a matrix for MREs was investigated. Pureprena or Deproteinised Natural Rubber (DPNR) is a specialty natural rubber that has good dynamic properties, particularly with respect to damping parameters. DPNR was compounded with 60 wt% of CIPs to fabricate MREs. The performance of the DPNR-based MRE was measured in terms of tensile strength, dynamic properties, and magnetorheological (MR) effect and compared with polyisoprene (IR)-based MRE with the same amount of CIPs. Dynamic Mechanical Analyzer (DMA) showed that the loss factor in the glass transition region of the DPNR-based MRE was higher than that of the IR-based MRE, indicating better damping properties. Further investigation was undertaken using a servo-hydraulic testing machine to characterise the effect of strain amplitude and frequency on the dynamic properties (e.g. damping coefficient) of MREs at zero magnetic fields. The results demonstrate that DPNR-based MREs possess a comparable damping coefficient to that of IR-based MREs. In addition, MR effect, which relates to the ratio between elastic modulus with applied magnetic field (on-state) to the same modulus without applied fields (off-state), was measured using a parallel plate rheometer. As a result, DPNR-based MREs have improved MR effect than that of IR-based MREs. Moreover, variable stiffness is obtained when the magnetic field was increased to 0.8T. Loss factor or tan δ of MREs was found to vary against different magnetic fields. Finally, MREs with varied stiffness and damping were found to have potential as active control devices for smart damping materials.