Novel Design of Superhydrophobic and Anticorrosive PTFE and PAA + β - CD Composite Coating Deposited by Electrospinning, Spin Coating and Electrospraying Techniques
A superhydrophobic composite coating consisting of polytetrafluoroethylene (PTFE) and poly(acrylic acid)+ β-cyclodextrin (PAA + β-CD) was prepared on an aluminum alloy AA 6061T6 substrate by a three-step process of electrospinnig, spin coating, and electrospraying. The electrospinning technique is u...
Gespeichert in:
Veröffentlicht in: | Polymers 2022-10, Vol.14 (20), p.4356 |
---|---|
Hauptverfasser: | , , , , , , , |
Format: | Artikel |
Sprache: | eng |
Schlagworte: | |
Online-Zugang: | Volltext |
Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
Zusammenfassung: | A superhydrophobic composite coating consisting of polytetrafluoroethylene (PTFE) and poly(acrylic acid)+ β-cyclodextrin (PAA + β-CD) was prepared on an aluminum alloy AA 6061T6 substrate by a three-step process of electrospinnig, spin coating, and electrospraying. The electrospinning technique is used for the fabrication of a polymeric binder layer synthesized from PAA + β-CD. The superhydrophilic characteristic of the electrospun PAA + β-CD layer makes it suitable for the absorption of an aqueous suspension with PTFE particles in a spin-coating process, obtaining a hydrophobic behavior. Then, the electrospraying of a modified PTFE dispersion forms a layer of distributed PTFE particles, in which a strong bonding of the particles with each other and with the PTFE particles fixed in the PAA + β-CD fiber matrix results in a remarkable improvement of the particles adhesion to the substrate by different heat treatments. The experimental results corroborate the important role of obtaining hierarchical micro/nano multilevel structures for the optimization of superhydrophobic surfaces, leading to water contact angles above 170°, very low contact angle of hysteresis (CAH = 2°) and roll-off angle (αroll−off < 5°). In addition, a superior corrosion resistance is obtained, generating a barrier to retain the electrolyte infiltration. This study may provide useful insights for a wide range of applications. |
---|---|
ISSN: | 2073-4360 2073-4360 |
DOI: | 10.3390/polym14204356 |