Investigation of water sorption and aluminum releases from high viscosity and resin modified glass ionomer

High viscosity glass ionomer cement (HVGIC) and resin-modified glass ionomer cement (RMGIC) have recently been clinically preferred thanks to their numerous advantages. However, initial moisture contamination has a negative effect on the mechanical and physical properties of these cements. The aim of this study was of HVGICs and RMGICs, with and without surface protection, on water sorption, solubility and release of aluminum. In this study, as HVGICs; Equia Forte, IonoStar Plus, Riva Self Cure; as RMCIS, Ionolux and Riva Light Cure; and as control, Z250 universal composite was used. Equia coat, Voco varnish and Riva coat were chosen as surface protective. Water sorption and solubility levels of the samples were measured according to ISO 4049:2009. Al levels released from samples were determined by graphite furnace atomic absorption spectroscopy (GFAAS) for 7, 14 and 21 days. Statistical evaluation of the results was made using one-way variance analysis (ANOVA) and Tukey post-hoc test (