Microscopic Features of Fractured Fragment of Nickel-Titanium Endodontic Instruments by Two Different Modes of Torsional Loading

This study compared the microscopic features of the fractured endodontic nickel-titanium (NiTi) rotary instruments by two different torsional loadings: repetitive torsional loading (RTL) and single torsional loading (STL) based on the International Organization for Standardization (ISO). ProTaper Ne...

Ausführliche Beschreibung

Gespeichert in:

Bibliographische Detailangaben
Veröffentlicht in:	Scanning 2018-01, Vol.2018 (2018), p.1-5
Hauptverfasser:	Kim, Hyeon-Cheol, Ha, Jung-Hong, Kwak, Sang Won, Abu-Tahun, Ibrahim H.
Format:	Artikel
Sprache:	eng
Schlagworte:	Abrasion Alloys Crack propagation Dimpling Fatigue cracks Fatigue failure Fracture mechanics Load Mechanical properties Metal fatigue Nickel Scanning electron microscopy Standardization Titanium Topography Torsion Variance analysis
Online-Zugang:	Volltext
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!

Schreiben Sie den ersten Kommentar!