Assessment of changes in color and color parameters of light-cured composite resin after alternative polymerization methods

ABSTRACT Objective:To examine the amount of change in color and color parameters of a composite resin (Filtek P60) polymerized by five different polymerization methods. Methods: A Teflon mold (6mm in diameter, 2mm in height) was used to prepare the composite resin discs (n=10). G1: Polymerization with inlay oven; G2: Polymerization with HQTH and autoclave; G3: Polymerization with LED and autoclave; G4: Polymerization with HQTH; G5: Polymerization with LED. Colorimetric values of the specimens before and after polymerization were measured using a spectrophotometer. The CIE L*a*b color system was used for the determination of color difference. Analysis of variance (ANOVA) was used to analyze the data for significant differences. Tukey’s HSD test and paired two-tailed tests were used to perform multiple comparisons (α=.05). Results: There were no significant differences in total color change (ΔE*ab) among the polymerization groups (P>.05). However, the lowest color change (ΔE*ab) value was 3.3 in LED and autoclave; the highest color change (ΔE*ab) value was 4.6 in HQTH. For all groups, CIE L*, C*ab and a*values decreased after polymerization (P