Influence of Operating Temperature on Crack Growth Characteristics and Fatigue Life Prediction of Carbon Black-Filled Hydrogenated Nitrile Butadiene Rubber

Rubber is widely used in situations involving cyclic loads, and the influence of temperature on rubber properties is particularly pronounced under cyclic loading. In this study, mechanical property tests and crack propagation tests of carbon black-filled hydrogenated nitrile butadiene rubber were co...

Ausführliche Beschreibung

Gespeichert in:

Bibliographische Detailangaben
Veröffentlicht in:	Polymers 2024-12, Vol.16 (24), p.3574
Hauptverfasser:	Li, Runze, Lian, Zisheng, Wei, Wensheng
Format:	Artikel
Sprache:	eng
Schlagworte:	Aging Analysis Butadiene Carbon Carbon black Crack propagation Cyclic loads Energy Fatigue cracks Fatigue failure Fatigue life Fatigue tests Fracture mechanics Growth Hydrogenation Investigations Life prediction Nitrile rubber Operating temperature Parameters Prediction models Propagation Rubber Rubber industry Shear strain Strain energy Temperature Temperature dependence
Online-Zugang:	Volltext
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!

Schreiben Sie den ersten Kommentar!