Experimental Test Results from an Environmental Protection Agency Test Method for Determination of Vapor Suppressant Effectiveness

The results obtained from laboratory experiments conducted using Environmental Protection Agency (EPA) subpart WWWW of 40 Code of Federal Regulations (CFR) part 63 (1)-test method are discussed in this article. The original test method was developed to measure the effectiveness of wax suppressants u...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Journal of materials engineering and performance 2005-04, Vol.14 (2), p.229-235
Hauptverfasser: Tock, Richard W, Ahern, Daniel W
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:The results obtained from laboratory experiments conducted using Environmental Protection Agency (EPA) subpart WWWW of 40 Code of Federal Regulations (CFR) part 63 (1)-test method are discussed in this article. The original test method was developed to measure the effectiveness of wax suppressants used to reduce hazardous air pollutant (HAP) emissions from unsaturated polyester (UP)/vinyl ester resins. Wax additions of 1.5% by weight to commercial UP resins suppress HAP emissions through the formation of surface barrier films. However, the tests performed in this study included the use of limestone and an adjunct, organic fiber reinforcement, rather than the wax. The addition of either commercial product to the UP formulations tested in this study was also shown to reduce HAP emissions. Suppression was a combination of absorption and an increased diffusion path barrier for the volatile organic carbon (VOC) components. Based on the limited data obtained, it was shown that the oil absorption characteristics of the two adjunct products could be used to estimate the expected level of vapor suppression for a specific resin formulation. Values reported in the literature for the oil adsorption characteristics of the adjunct limestone and the commercial biomass fiber were used in the laboratory tests. Although the oil adsorption characteristic of any ingredient added to a base resin formulation is indicative of its potential for emissions reduction, the EPA test protocol is still required to be performed for validation. Such screening tests will always be needed due to the variability associated with commercial UP resins and the evolution of customized UP/fiberglass composite formulations developed by custom molding shops.[PUBLICATION ABSTRACT]
ISSN:1059-9495
1544-1024
DOI:10.1361/10599490523292