Influence of Bond Coat Roughness on Life Time of APS Thermal Barrier Coating Systems under Thermo-Mechanical Load

The influence of the bond coat roughness on the life time of air plasma-sprayed (APS) thermal barrier coating systems (TBCs) was investigated under thermo-mechanical (TMF) load. The TBC system was applied on hollow cylindrical specimens made of the single crystal super alloy CMSX-4 in the orientatio...

Ausführliche Beschreibung

Bibliographische Detailangaben

Veröffentlicht in:	Journal of Solid Mechanics and Materials Engineering 2010, Vol.4(2), pp.208-220
Hauptverfasser:	SCHMIDT, Andreas, ALEKSANOGLU, Herman, MAO, Tongsheng, SCHOLZ, Alfred, BERGER, Christina
Format:	Artikel
Sprache:	eng
Schlagworte:	Air Plasma Sprayed Alloy systems Bond Coat Roughness Bonding Coating Crack Initiation Crack Propagation Delaminating Fracture mechanics Roughness Thermal Barrier Coating System Thermal barrier coatings Thermally Grown Oxide Layer Thermo-Mechanical Fatigue
Online-Zugang:	Volltext
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!