The corrosion behaviour of WC-VC-Co hardmetals in acidic media

The effect of increasing vanadium carbide (VC) content on the corrosion behaviour of tungsten carbide – 10 wt% cobalt hardmetals was investigated in 1 M hydrochloric (HCl), and sulphuric (H 2SO 4) acids solutions. Increasing VC content makes the open circuit potential (OCP) in the test solutions mor...

Ausführliche Beschreibung

Gespeichert in:

Bibliographische Detailangaben
Veröffentlicht in:	Corrosion science 2010-09, Vol.52 (9), p.3118-3125
Hauptverfasser:	Konadu, D.S., Merwe, J. van der, Potgieter, J.H., Potgieter-Vermaak, S., Machio, C.N.
Format:	Artikel
Sprache:	eng
Schlagworte:	A. WC-Co A. WC-VC-Co Applied sciences B. Polarization B. Raman spectroscopy B. XRD C. Passivity Cemented carbides Cobalt Corrosion Corrosion effects Corrosion environments Current density Exact sciences and technology Hydrochloric acid Metals. Metallurgy Open circuit potential Sulfates Tungsten oxides
Online-Zugang:	Volltext
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!

Schreiben Sie den ersten Kommentar!