Effect of calcium sulfate particles on corrosion and erosion-corrosion of carbon steel
In laboratory erosion-corrosion and corrosion experiments it was determined that calcium sulfate which occurs in fluidized bed combustion materials from the reaction of calcined limestone with the sulfur in the coal fuel can either protect the base metal against erosion-corrosion by aiding the forma...
Gespeichert in:
| Veröffentlicht in: | Wear 1992-01, Vol.155 (1), p.149-161 |
|---|---|
| Hauptverfasser: | , , |
| Format: | Artikel |
| Sprache: | eng |
| Schlagworte: | |
| Online-Zugang: | Volltext |
| Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
| container_end_page | 161 |
|---|---|
| container_issue | 1 |
| container_start_page | 149 |
| container_title | Wear |
| container_volume | 155 |
| creator | Geng, G.Q. Wang, B.Q. Levy, A.V. |
| description | In laboratory erosion-corrosion and corrosion experiments it was determined that calcium sulfate which occurs in fluidized bed combustion materials from the reaction of calcined limestone with the sulfur in the coal fuel can either protect the base metal against erosion-corrosion by aiding the formation of mixed calcium-compound-iron-oxide layers on the surface or promote its sulfidation, depending on the calcium sulfate content of the erodent particles and the test temperature, particle velocity, and duration. The reaction between calcium sulfate particles and metal substrates produced iron sulfide under certain test conditions. |
| doi_str_mv | 10.1016/0043-1648(92)90115-O |
| format | Article |
| fullrecord | <record><control><sourceid>proquest_cross</sourceid><recordid>TN_cdi_proquest_miscellaneous_744567056</recordid><sourceformat>XML</sourceformat><sourcesystem>PC</sourcesystem><els_id>004316489290115O</els_id><sourcerecordid>744567056</sourcerecordid><originalsourceid>FETCH-LOGICAL-c463t-729675d5ea71f5f77514f49ff772f8648c9fbb0cc008b72c82ba0ef3fbd0a7bd3</originalsourceid><addsrcrecordid>eNqNkUtLxDAUhYMoOI7-AxddiI9FNUnzaDaCDOMDBmajbkOa3kCk045JR_Dfm05l3A1CIIfwnXvDOQidE3xLMBF3GLMiJ4KV14reKEwIz5cHaEJKWeSUS3mIJjvkGJ3E-IExJoqLCXqfOwe2zzqXWdNYv1llcdM400O2NqH3toGYdW1muxC66JMybZ3BqPO_160_VEnFHqA5RUfONBHOfu8penucv86e88Xy6WX2sMgtE0WfS6qE5DUHI4njTkpOmGPKJUVdmX5rlasqbC3GZSWpLWllMLjCVTU2sqqLKboa565D97mB2OuVjxaaxrTQbaKWjHEhMReJvNxLUi6Go_4JkiKBbARtyiAGcHod_MqEb02wHnrRQ-h6CF0rqre96GWyXfzONzFF7oJprY87LysIY3iYfj9ikOL78hB0tB5aC7UPqTBdd37_nh8aTaG0</addsrcrecordid><sourcetype>Aggregation Database</sourcetype><iscdi>true</iscdi><recordtype>article</recordtype><pqid>25625613</pqid></control><display><type>article</type><title>Effect of calcium sulfate particles on corrosion and erosion-corrosion of carbon steel</title><source>Access via ScienceDirect (Elsevier)</source><creator>Geng, G.Q. ; Wang, B.Q. ; Levy, A.V.</creator><creatorcontrib>Geng, G.Q. ; Wang, B.Q. ; Levy, A.V.</creatorcontrib><description>In laboratory erosion-corrosion and corrosion experiments it was determined that calcium sulfate which occurs in fluidized bed combustion materials from the reaction of calcined limestone with the sulfur in the coal fuel can either protect the base metal against erosion-corrosion by aiding the formation of mixed calcium-compound-iron-oxide layers on the surface or promote its sulfidation, depending on the calcium sulfate content of the erodent particles and the test temperature, particle velocity, and duration. The reaction between calcium sulfate particles and metal substrates produced iron sulfide under certain test conditions.</description><identifier>ISSN: 0043-1648</identifier><identifier>EISSN: 1873-2577</identifier><identifier>DOI: 10.1016/0043-1648(92)90115-O</identifier><identifier>CODEN: WEARAH</identifier><language>eng</language><publisher>Lausanne: Elsevier B.V</publisher><subject>Applied sciences ; Corrosion ; Corrosion mechanisms ; erosion ; Exact sciences and technology ; Metals. Metallurgy</subject><ispartof>Wear, 1992-01, Vol.155 (1), p.149-161</ispartof><rights>1992</rights><rights>1993 INIST-CNRS</rights><lds50>peer_reviewed</lds50><woscitedreferencessubscribed>false</woscitedreferencessubscribed><citedby>FETCH-LOGICAL-c463t-729675d5ea71f5f77514f49ff772f8648c9fbb0cc008b72c82ba0ef3fbd0a7bd3</citedby><cites>FETCH-LOGICAL-c463t-729675d5ea71f5f77514f49ff772f8648c9fbb0cc008b72c82ba0ef3fbd0a7bd3</cites></display><links><openurl>$$Topenurl_article</openurl><openurlfulltext>$$Topenurlfull_article</openurlfulltext><thumbnail>$$Tsyndetics_thumb_exl</thumbnail><linktohtml>$$Uhttps://dx.doi.org/10.1016/0043-1648(92)90115-O$$EHTML$$P50$$Gelsevier$$H</linktohtml><link.rule.ids>314,780,784,3550,27924,27925,45995</link.rule.ids><backlink>$$Uhttp://pascal-francis.inist.fr/vibad/index.php?action=getRecordDetail&idt=4314403$$DView record in Pascal Francis$$Hfree_for_read</backlink></links><search><creatorcontrib>Geng, G.Q.</creatorcontrib><creatorcontrib>Wang, B.Q.</creatorcontrib><creatorcontrib>Levy, A.V.</creatorcontrib><title>Effect of calcium sulfate particles on corrosion and erosion-corrosion of carbon steel</title><title>Wear</title><description>In laboratory erosion-corrosion and corrosion experiments it was determined that calcium sulfate which occurs in fluidized bed combustion materials from the reaction of calcined limestone with the sulfur in the coal fuel can either protect the base metal against erosion-corrosion by aiding the formation of mixed calcium-compound-iron-oxide layers on the surface or promote its sulfidation, depending on the calcium sulfate content of the erodent particles and the test temperature, particle velocity, and duration. The reaction between calcium sulfate particles and metal substrates produced iron sulfide under certain test conditions.</description><subject>Applied sciences</subject><subject>Corrosion</subject><subject>Corrosion mechanisms</subject><subject>erosion</subject><subject>Exact sciences and technology</subject><subject>Metals. Metallurgy</subject><issn>0043-1648</issn><issn>1873-2577</issn><fulltext>true</fulltext><rsrctype>article</rsrctype><creationdate>1992</creationdate><recordtype>article</recordtype><recordid>eNqNkUtLxDAUhYMoOI7-AxddiI9FNUnzaDaCDOMDBmajbkOa3kCk045JR_Dfm05l3A1CIIfwnXvDOQidE3xLMBF3GLMiJ4KV14reKEwIz5cHaEJKWeSUS3mIJjvkGJ3E-IExJoqLCXqfOwe2zzqXWdNYv1llcdM400O2NqH3toGYdW1muxC66JMybZ3BqPO_160_VEnFHqA5RUfONBHOfu8penucv86e88Xy6WX2sMgtE0WfS6qE5DUHI4njTkpOmGPKJUVdmX5rlasqbC3GZSWpLWllMLjCVTU2sqqLKboa565D97mB2OuVjxaaxrTQbaKWjHEhMReJvNxLUi6Go_4JkiKBbARtyiAGcHod_MqEb02wHnrRQ-h6CF0rqre96GWyXfzONzFF7oJprY87LysIY3iYfj9ikOL78hB0tB5aC7UPqTBdd37_nh8aTaG0</recordid><startdate>19920101</startdate><enddate>19920101</enddate><creator>Geng, G.Q.</creator><creator>Wang, B.Q.</creator><creator>Levy, A.V.</creator><general>Elsevier B.V</general><general>Elsevier Science</general><scope>IQODW</scope><scope>AAYXX</scope><scope>CITATION</scope><scope>7U5</scope><scope>8FD</scope><scope>L7M</scope><scope>8BQ</scope><scope>JG9</scope><scope>7TC</scope></search><sort><creationdate>19920101</creationdate><title>Effect of calcium sulfate particles on corrosion and erosion-corrosion of carbon steel</title><author>Geng, G.Q. ; Wang, B.Q. ; Levy, A.V.</author></sort><facets><frbrtype>5</frbrtype><frbrgroupid>cdi_FETCH-LOGICAL-c463t-729675d5ea71f5f77514f49ff772f8648c9fbb0cc008b72c82ba0ef3fbd0a7bd3</frbrgroupid><rsrctype>articles</rsrctype><prefilter>articles</prefilter><language>eng</language><creationdate>1992</creationdate><topic>Applied sciences</topic><topic>Corrosion</topic><topic>Corrosion mechanisms</topic><topic>erosion</topic><topic>Exact sciences and technology</topic><topic>Metals. Metallurgy</topic><toplevel>peer_reviewed</toplevel><toplevel>online_resources</toplevel><creatorcontrib>Geng, G.Q.</creatorcontrib><creatorcontrib>Wang, B.Q.</creatorcontrib><creatorcontrib>Levy, A.V.</creatorcontrib><collection>Pascal-Francis</collection><collection>CrossRef</collection><collection>Solid State and Superconductivity Abstracts</collection><collection>Technology Research Database</collection><collection>Advanced Technologies Database with Aerospace</collection><collection>METADEX</collection><collection>Materials Research Database</collection><collection>Mechanical Engineering Abstracts</collection><jtitle>Wear</jtitle></facets><delivery><delcategory>Remote Search Resource</delcategory><fulltext>fulltext</fulltext></delivery><addata><au>Geng, G.Q.</au><au>Wang, B.Q.</au><au>Levy, A.V.</au><format>journal</format><genre>article</genre><ristype>JOUR</ristype><atitle>Effect of calcium sulfate particles on corrosion and erosion-corrosion of carbon steel</atitle><jtitle>Wear</jtitle><date>1992-01-01</date><risdate>1992</risdate><volume>155</volume><issue>1</issue><spage>149</spage><epage>161</epage><pages>149-161</pages><issn>0043-1648</issn><eissn>1873-2577</eissn><coden>WEARAH</coden><abstract>In laboratory erosion-corrosion and corrosion experiments it was determined that calcium sulfate which occurs in fluidized bed combustion materials from the reaction of calcined limestone with the sulfur in the coal fuel can either protect the base metal against erosion-corrosion by aiding the formation of mixed calcium-compound-iron-oxide layers on the surface or promote its sulfidation, depending on the calcium sulfate content of the erodent particles and the test temperature, particle velocity, and duration. The reaction between calcium sulfate particles and metal substrates produced iron sulfide under certain test conditions.</abstract><cop>Lausanne</cop><cop>Amsterdam</cop><cop>New York, NY</cop><pub>Elsevier B.V</pub><doi>10.1016/0043-1648(92)90115-O</doi><tpages>13</tpages></addata></record> |
| fulltext | fulltext |
| identifier | ISSN: 0043-1648 |
| ispartof | Wear, 1992-01, Vol.155 (1), p.149-161 |
| issn | 0043-1648 1873-2577 |
| language | eng |
| recordid | cdi_proquest_miscellaneous_744567056 |
| source | Access via ScienceDirect (Elsevier) |
| subjects | Applied sciences Corrosion Corrosion mechanisms erosion Exact sciences and technology Metals. Metallurgy |
| title | Effect of calcium sulfate particles on corrosion and erosion-corrosion of carbon steel |
| url | https://sfx.bib-bvb.de/sfx_tum?ctx_ver=Z39.88-2004&ctx_enc=info:ofi/enc:UTF-8&ctx_tim=2024-12-29T20%3A10%3A22IST&url_ver=Z39.88-2004&url_ctx_fmt=infofi/fmt:kev:mtx:ctx&rfr_id=info:sid/primo.exlibrisgroup.com:primo3-Article-proquest_cross&rft_val_fmt=info:ofi/fmt:kev:mtx:journal&rft.genre=article&rft.atitle=Effect%20of%20calcium%20sulfate%20particles%20on%20corrosion%20and%20erosion-corrosion%20of%20carbon%20steel&rft.jtitle=Wear&rft.au=Geng,%20G.Q.&rft.date=1992-01-01&rft.volume=155&rft.issue=1&rft.spage=149&rft.epage=161&rft.pages=149-161&rft.issn=0043-1648&rft.eissn=1873-2577&rft.coden=WEARAH&rft_id=info:doi/10.1016/0043-1648(92)90115-O&rft_dat=%3Cproquest_cross%3E744567056%3C/proquest_cross%3E%3Curl%3E%3C/url%3E&disable_directlink=true&sfx.directlink=off&sfx.report_link=0&rft_id=info:oai/&rft_pqid=25625613&rft_id=info:pmid/&rft_els_id=004316489290115O&rfr_iscdi=true |