Erosion-corrosion of mild steel. (2nd Report, Effect of pH and Cl ions)
The effects of pH and Cl ion concentration on erosion-corrosion of mild steel in aqueous solutions were investigated using an impingement jet flow apparatus. It was found that the mass loss in ion-exchange water decreased with jet velocity, and the mass loss in the water with 6.7 ppmCl reached a pea...
Gespeichert in:
| Veröffentlicht in: | Nihon Kikai Gakkai rombunshuu. B hen 1989, Vol.55 (518), p.3000-3005 |
|---|---|
| Hauptverfasser: | , , , |
| Format: | Artikel |
| Sprache: | eng ; jpn |
| Schlagworte: | |
| Online-Zugang: | Volltext |
| Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
| container_end_page | 3005 |
|---|---|
| container_issue | 518 |
| container_start_page | 3000 |
| container_title | Nihon Kikai Gakkai rombunshuu. B hen |
| container_volume | 55 |
| creator | MANJO, Hiroshi KURATA, Yoshiaki ASANO, Osamu SANADA, Norio |
| description | The effects of pH and Cl ion concentration on erosion-corrosion of mild steel in aqueous solutions were investigated using an impingement jet flow apparatus. It was found that the mass loss in ion-exchange water decreased with jet velocity, and the mass loss in the water with 6.7 ppmCl reached a peak at 0.1 m/s. Such a peak appeared in the case of the other solutions, but the peak value depended on pH, and was absent when pH > 6.5, because the increase of pH suppressed the breakdown effect of the Cl ion. A large number of pits were generated on the mild steel subjected to the solutions with Cl ions, probably because the Cl ions caused breakdown of parts of the protective film. |
| doi_str_mv | 10.1299/kikaib.55.3000 |
| format | Article |
| fullrecord | <record><control><sourceid>proquest_cross</sourceid><recordid>TN_cdi_proquest_miscellaneous_744565437</recordid><sourceformat>XML</sourceformat><sourcesystem>PC</sourcesystem><sourcerecordid>744565437</sourcerecordid><originalsourceid>FETCH-LOGICAL-c2810-725e96100b70eedb6bce461c2c775893390db93ba40816bc2d46572f769cba3a3</originalsourceid><addsrcrecordid>eNotkM1LAzEQxYMoWLRXz7mp4K6T781RSm2FgiB6Dkk2C2u3zZpsD_73pqynGXi_mXnzELojUBOq9fO-39ve1ULUDAAu0II0Da8axuUlWgBrVCWAyGu0zPm7ACChISAXaLNOMffxWPmY5g7HDh_6ocV5CmGo8QM9tvgjjDFNT3jddcFPZ2TcYluE1YDLTH68RVedHXJY_tcb9PW6_lxtq9375m31sqs8LQcrRUXQkgA4BSG0TjofuCSeeqVEoxnT0DrNnOXFXxFpy6VQtFNSe2eZZTfoft47pvhzCnkyhz77MAz2GOIpG8W5kIIzVch6Jn35K6fQmTH1B5t-DQFzzszMmRkhzDkz9gf1ol3B</addsrcrecordid><sourcetype>Aggregation Database</sourcetype><iscdi>true</iscdi><recordtype>article</recordtype><pqid>744565437</pqid></control><display><type>article</type><title>Erosion-corrosion of mild steel. (2nd Report, Effect of pH and Cl ions)</title><source>J-STAGE (Japan Science & Technology Information Aggregator, Electronic) Freely Available Titles - Japanese</source><source>EZB-FREE-00999 freely available EZB journals</source><creator>MANJO, Hiroshi ; KURATA, Yoshiaki ; ASANO, Osamu ; SANADA, Norio</creator><creatorcontrib>MANJO, Hiroshi ; KURATA, Yoshiaki ; ASANO, Osamu ; SANADA, Norio</creatorcontrib><description>The effects of pH and Cl ion concentration on erosion-corrosion of mild steel in aqueous solutions were investigated using an impingement jet flow apparatus. It was found that the mass loss in ion-exchange water decreased with jet velocity, and the mass loss in the water with 6.7 ppmCl reached a peak at 0.1 m/s. Such a peak appeared in the case of the other solutions, but the peak value depended on pH, and was absent when pH > 6.5, because the increase of pH suppressed the breakdown effect of the Cl ion. A large number of pits were generated on the mild steel subjected to the solutions with Cl ions, probably because the Cl ions caused breakdown of parts of the protective film.</description><identifier>ISSN: 0387-5016</identifier><identifier>EISSN: 1884-8346</identifier><identifier>DOI: 10.1299/kikaib.55.3000</identifier><language>eng ; jpn</language><subject>corrosion ; erosion ; steel</subject><ispartof>Nihon Kikai Gakkai rombunshuu. B hen, 1989, Vol.55 (518), p.3000-3005</ispartof><oa>free_for_read</oa><woscitedreferencessubscribed>false</woscitedreferencessubscribed><citedby>FETCH-LOGICAL-c2810-725e96100b70eedb6bce461c2c775893390db93ba40816bc2d46572f769cba3a3</citedby></display><links><openurl>$$Topenurl_article</openurl><openurlfulltext>$$Topenurlfull_article</openurlfulltext><thumbnail>$$Tsyndetics_thumb_exl</thumbnail><link.rule.ids>314,776,780,4009,27902,27903,27904</link.rule.ids></links><search><creatorcontrib>MANJO, Hiroshi</creatorcontrib><creatorcontrib>KURATA, Yoshiaki</creatorcontrib><creatorcontrib>ASANO, Osamu</creatorcontrib><creatorcontrib>SANADA, Norio</creatorcontrib><title>Erosion-corrosion of mild steel. (2nd Report, Effect of pH and Cl ions)</title><title>Nihon Kikai Gakkai rombunshuu. B hen</title><description>The effects of pH and Cl ion concentration on erosion-corrosion of mild steel in aqueous solutions were investigated using an impingement jet flow apparatus. It was found that the mass loss in ion-exchange water decreased with jet velocity, and the mass loss in the water with 6.7 ppmCl reached a peak at 0.1 m/s. Such a peak appeared in the case of the other solutions, but the peak value depended on pH, and was absent when pH > 6.5, because the increase of pH suppressed the breakdown effect of the Cl ion. A large number of pits were generated on the mild steel subjected to the solutions with Cl ions, probably because the Cl ions caused breakdown of parts of the protective film.</description><subject>corrosion</subject><subject>erosion</subject><subject>steel</subject><issn>0387-5016</issn><issn>1884-8346</issn><fulltext>true</fulltext><rsrctype>article</rsrctype><creationdate>1989</creationdate><recordtype>article</recordtype><recordid>eNotkM1LAzEQxYMoWLRXz7mp4K6T781RSm2FgiB6Dkk2C2u3zZpsD_73pqynGXi_mXnzELojUBOq9fO-39ve1ULUDAAu0II0Da8axuUlWgBrVCWAyGu0zPm7ACChISAXaLNOMffxWPmY5g7HDh_6ocV5CmGo8QM9tvgjjDFNT3jddcFPZ2TcYluE1YDLTH68RVedHXJY_tcb9PW6_lxtq9375m31sqs8LQcrRUXQkgA4BSG0TjofuCSeeqVEoxnT0DrNnOXFXxFpy6VQtFNSe2eZZTfoft47pvhzCnkyhz77MAz2GOIpG8W5kIIzVch6Jn35K6fQmTH1B5t-DQFzzszMmRkhzDkz9gf1ol3B</recordid><startdate>1989</startdate><enddate>1989</enddate><creator>MANJO, Hiroshi</creator><creator>KURATA, Yoshiaki</creator><creator>ASANO, Osamu</creator><creator>SANADA, Norio</creator><scope>AAYXX</scope><scope>CITATION</scope><scope>7TC</scope></search><sort><creationdate>1989</creationdate><title>Erosion-corrosion of mild steel. (2nd Report, Effect of pH and Cl ions)</title><author>MANJO, Hiroshi ; KURATA, Yoshiaki ; ASANO, Osamu ; SANADA, Norio</author></sort><facets><frbrtype>5</frbrtype><frbrgroupid>cdi_FETCH-LOGICAL-c2810-725e96100b70eedb6bce461c2c775893390db93ba40816bc2d46572f769cba3a3</frbrgroupid><rsrctype>articles</rsrctype><prefilter>articles</prefilter><language>eng ; jpn</language><creationdate>1989</creationdate><topic>corrosion</topic><topic>erosion</topic><topic>steel</topic><toplevel>online_resources</toplevel><creatorcontrib>MANJO, Hiroshi</creatorcontrib><creatorcontrib>KURATA, Yoshiaki</creatorcontrib><creatorcontrib>ASANO, Osamu</creatorcontrib><creatorcontrib>SANADA, Norio</creatorcontrib><collection>CrossRef</collection><collection>Mechanical Engineering Abstracts</collection><jtitle>Nihon Kikai Gakkai rombunshuu. B hen</jtitle></facets><delivery><delcategory>Remote Search Resource</delcategory><fulltext>fulltext</fulltext></delivery><addata><au>MANJO, Hiroshi</au><au>KURATA, Yoshiaki</au><au>ASANO, Osamu</au><au>SANADA, Norio</au><format>journal</format><genre>article</genre><ristype>JOUR</ristype><atitle>Erosion-corrosion of mild steel. (2nd Report, Effect of pH and Cl ions)</atitle><jtitle>Nihon Kikai Gakkai rombunshuu. B hen</jtitle><date>1989</date><risdate>1989</risdate><volume>55</volume><issue>518</issue><spage>3000</spage><epage>3005</epage><pages>3000-3005</pages><issn>0387-5016</issn><eissn>1884-8346</eissn><abstract>The effects of pH and Cl ion concentration on erosion-corrosion of mild steel in aqueous solutions were investigated using an impingement jet flow apparatus. It was found that the mass loss in ion-exchange water decreased with jet velocity, and the mass loss in the water with 6.7 ppmCl reached a peak at 0.1 m/s. Such a peak appeared in the case of the other solutions, but the peak value depended on pH, and was absent when pH > 6.5, because the increase of pH suppressed the breakdown effect of the Cl ion. A large number of pits were generated on the mild steel subjected to the solutions with Cl ions, probably because the Cl ions caused breakdown of parts of the protective film.</abstract><doi>10.1299/kikaib.55.3000</doi><tpages>6</tpages><oa>free_for_read</oa></addata></record> |
| fulltext | fulltext |
| identifier | ISSN: 0387-5016 |
| ispartof | Nihon Kikai Gakkai rombunshuu. B hen, 1989, Vol.55 (518), p.3000-3005 |
| issn | 0387-5016 1884-8346 |
| language | eng ; jpn |
| recordid | cdi_proquest_miscellaneous_744565437 |
| source | J-STAGE (Japan Science & Technology Information Aggregator, Electronic) Freely Available Titles - Japanese; EZB-FREE-00999 freely available EZB journals |
| subjects | corrosion erosion steel |
| title | Erosion-corrosion of mild steel. (2nd Report, Effect of pH and Cl ions) |
| url | https://sfx.bib-bvb.de/sfx_tum?ctx_ver=Z39.88-2004&ctx_enc=info:ofi/enc:UTF-8&ctx_tim=2025-01-24T02%3A39%3A16IST&url_ver=Z39.88-2004&url_ctx_fmt=infofi/fmt:kev:mtx:ctx&rfr_id=info:sid/primo.exlibrisgroup.com:primo3-Article-proquest_cross&rft_val_fmt=info:ofi/fmt:kev:mtx:journal&rft.genre=article&rft.atitle=Erosion-corrosion%20of%20mild%20steel.%20(2nd%20Report,%20Effect%20of%20pH%20and%20Cl%20ions)&rft.jtitle=Nihon%20Kikai%20Gakkai%20rombunshuu.%20B%20hen&rft.au=MANJO,%20Hiroshi&rft.date=1989&rft.volume=55&rft.issue=518&rft.spage=3000&rft.epage=3005&rft.pages=3000-3005&rft.issn=0387-5016&rft.eissn=1884-8346&rft_id=info:doi/10.1299/kikaib.55.3000&rft_dat=%3Cproquest_cross%3E744565437%3C/proquest_cross%3E%3Curl%3E%3C/url%3E&disable_directlink=true&sfx.directlink=off&sfx.report_link=0&rft_id=info:oai/&rft_pqid=744565437&rft_id=info:pmid/&rfr_iscdi=true |