Failure Strength of Woven Glass Fiber-Epoxy Composites Pinned Joints

In this paper, mechanical behavior and damage development of pin-loaded woven glass fiber-epoxy composites have been observed numerically and experimentally. Parametric studies have been performed to evaluate the effects of joint geometry and ply orientation on the failure strength and failure mode...

Ausführliche Beschreibung

Bibliographische Detailangaben

Veröffentlicht in:	Journal of composite materials 2003-08, Vol.37 (15), p.1337-1350
Hauptverfasser:	Içten, Bulent Murat, Okutan, Buket, Karakuzu, Ramazan
Format:	Artikel
Sprache:	eng
Schlagworte:	Applied sciences Composites Exact sciences and technology Forms of application and semi-finished materials Fracture mechanics (crack, fatigue, damage...) Fracture mechanics, fatigue and cracks Fundamental areas of phenomenology (including applications) Physics Polymer industry, paints, wood Solid mechanics Structural and continuum mechanics Technology of polymers
Online-Zugang:	Volltext
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!