Crack Initiation Behavior from Internal Defect in High Carbon-chromium Bearing Steel under Rolling Contact Fatigue

It is important to clarify the effects of nonmetallic inclusions on rolling contact fatigue life to extend or to predict the life of the rolling bearings. The observation of initial cracks from internal defects is desirable from this point of view. In this study, high carbon-chromium bearing steel,...

Ausführliche Beschreibung

Bibliographische Detailangaben

Veröffentlicht in:	Tetsu to hagane 2008/01/25, Vol.94(1), pp.13-20
Hauptverfasser:	Fujimatsu, Takeshi, Hiraoka, Kazuhiko, Yamamoto, Atsushi
Format:	Artikel
Sprache:	jpn
Schlagworte:	bearing steel fracture observation initial crack internal defect nonmetallic inclusion pore rolling contact fatigue life stress