Effect of microtexture on fatigue cracking in Ti–6Al–4V

Fatigue cracking in forged bar, unidirectionally rolled (UD) and cross-rolled (XR) plate product forms of Ti–6Al–4V subjected to high cycle fatigue with a stress ratio R = 0.3 was studied by examination of crack tips using electron backscatter diffraction (EBSD) and transmission electron microscopy...