Shape Control of Alumina Inclusions by Double Calcium Addition Treatment
Experimental and theoretical studies were carried out to clarify shape control of alumina inclusions during calcium double treatment in a line pipe steel for sour service. Calcium (Ca) double addition method were experimented by 280 t-scale commercial plant. In this method, Ca powder was firstly inj...
Gespeichert in:
| Veröffentlicht in: | Tetsu to hagane 2007/05/01, Vol.93(5), pp.355-361 |
|---|---|
| Hauptverfasser: | , , , |
| Format: | Artikel |
| Sprache: | jpn |
| Schlagworte: | |
| Online-Zugang: | Volltext |
| Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
| container_end_page | 361 |
|---|---|
| container_issue | 5 |
| container_start_page | 355 |
| container_title | Tetsu to hagane |
| container_volume | 93 |
| creator | ITO, Yo-ichi NARA, Seikoh KATO, Yoshiei SUDA, Mamoru |
| description | Experimental and theoretical studies were carried out to clarify shape control of alumina inclusions during calcium double treatment in a line pipe steel for sour service. Calcium (Ca) double addition method were experimented by 280 t-scale commercial plant. In this method, Ca powder was firstly injected for shape control of alumina inclusions by flux injection process (FI), and was secondly added for shape control of MnS to CaS in tundish of continuous casting machine after eliminating the first step Ca by RH degasser. The degree of shape control of alumina inclusions of this method was increased compared with that of the conventional Ca treatment by FI or tundish addition, and approaches to the equilibrium condition among Ca-CaO-Al2O3 system. To explain the shape control rate of alumina inclusions, the non-reacted core model fitted by the laboratory scale experimental results was applied for this experimental data. The calculated values from this model in the Ca double addition method agreed well with the observed ones. |
| doi_str_mv | 10.2355/tetsutohagane.93.355 |
| format | Article |
| fullrecord | <record><control><sourceid>proquest_cross</sourceid><recordid>TN_cdi_proquest_miscellaneous_29991904</recordid><sourceformat>XML</sourceformat><sourcesystem>PC</sourcesystem><sourcerecordid>29991904</sourcerecordid><originalsourceid>FETCH-LOGICAL-c394t-b27d4acdf632796a11f0ed940aef6058fadc61b7f3dab10a533a6e8993a1dea93</originalsourceid><addsrcrecordid>eNplkMtOwzAQRS0EEhX0D1hkxS7FjuMkXlbl0UqVWFDW1sSPNsiJi-0s-ve4CiAhNjOaO_dcaQahO4IXBWXsIeoYxugOsIdBLzhdJPECzUjT0LzgrLxEM4wLkhNWs2s0D6Fr01w2tKbFDK3fDnDU2coN0TubOZMt7dh3A2SbQdoxdG4IWXvKHt3Y2uQDK7uxz5ZKdTHtsp3XEHs9xFt0ZcAGPf_uN-j9-Wm3Wufb15fNarnNJeVlzNuiViVIZSpa1LwCQgzWipcYtKkwawwoWZG2NlRBSzAwSqHSDecUiNLA6Q26n3KP3n2OOkTRd0Fqa9P1bgyi4JwTjstkLCej9C4Er404-q4HfxIEi_PnxJ_PCU5FEhO2mbCPEGGvfyHwsZNW_4fYVM6BPx55AC_0QL8AFziCRg</addsrcrecordid><sourcetype>Aggregation Database</sourcetype><iscdi>true</iscdi><recordtype>article</recordtype><pqid>29991904</pqid></control><display><type>article</type><title>Shape Control of Alumina Inclusions by Double Calcium Addition Treatment</title><source>EZB Electronic Journals Library</source><source>J-STAGE</source><creator>ITO, Yo-ichi ; NARA, Seikoh ; KATO, Yoshiei ; SUDA, Mamoru</creator><creatorcontrib>ITO, Yo-ichi ; NARA, Seikoh ; KATO, Yoshiei ; SUDA, Mamoru</creatorcontrib><description>Experimental and theoretical studies were carried out to clarify shape control of alumina inclusions during calcium double treatment in a line pipe steel for sour service. Calcium (Ca) double addition method were experimented by 280 t-scale commercial plant. In this method, Ca powder was firstly injected for shape control of alumina inclusions by flux injection process (FI), and was secondly added for shape control of MnS to CaS in tundish of continuous casting machine after eliminating the first step Ca by RH degasser. The degree of shape control of alumina inclusions of this method was increased compared with that of the conventional Ca treatment by FI or tundish addition, and approaches to the equilibrium condition among Ca-CaO-Al2O3 system. To explain the shape control rate of alumina inclusions, the non-reacted core model fitted by the laboratory scale experimental results was applied for this experimental data. The calculated values from this model in the Ca double addition method agreed well with the observed ones.</description><identifier>ISSN: 0021-1575</identifier><identifier>EISSN: 1883-2954</identifier><identifier>DOI: 10.2355/tetsutohagane.93.355</identifier><language>jpn</language><publisher>The Iron and Steel Institute of Japan</publisher><subject>alumina inclusion ; calcium treatment ; shape control ; steelmaking</subject><ispartof>Tetsu-to-Hagane, 2007/05/01, Vol.93(5), pp.355-361</ispartof><rights>2007 The Iron and Steel Institute of Japan</rights><lds50>peer_reviewed</lds50><oa>free_for_read</oa><woscitedreferencessubscribed>false</woscitedreferencessubscribed><citedby>FETCH-LOGICAL-c394t-b27d4acdf632796a11f0ed940aef6058fadc61b7f3dab10a533a6e8993a1dea93</citedby><cites>FETCH-LOGICAL-c394t-b27d4acdf632796a11f0ed940aef6058fadc61b7f3dab10a533a6e8993a1dea93</cites></display><links><openurl>$$Topenurl_article</openurl><openurlfulltext>$$Topenurlfull_article</openurlfulltext><thumbnail>$$Tsyndetics_thumb_exl</thumbnail><link.rule.ids>314,780,784,1883,27924,27925</link.rule.ids></links><search><creatorcontrib>ITO, Yo-ichi</creatorcontrib><creatorcontrib>NARA, Seikoh</creatorcontrib><creatorcontrib>KATO, Yoshiei</creatorcontrib><creatorcontrib>SUDA, Mamoru</creatorcontrib><title>Shape Control of Alumina Inclusions by Double Calcium Addition Treatment</title><title>Tetsu to hagane</title><addtitle>Tetsu-to-Hagane</addtitle><description>Experimental and theoretical studies were carried out to clarify shape control of alumina inclusions during calcium double treatment in a line pipe steel for sour service. Calcium (Ca) double addition method were experimented by 280 t-scale commercial plant. In this method, Ca powder was firstly injected for shape control of alumina inclusions by flux injection process (FI), and was secondly added for shape control of MnS to CaS in tundish of continuous casting machine after eliminating the first step Ca by RH degasser. The degree of shape control of alumina inclusions of this method was increased compared with that of the conventional Ca treatment by FI or tundish addition, and approaches to the equilibrium condition among Ca-CaO-Al2O3 system. To explain the shape control rate of alumina inclusions, the non-reacted core model fitted by the laboratory scale experimental results was applied for this experimental data. The calculated values from this model in the Ca double addition method agreed well with the observed ones.</description><subject>alumina inclusion</subject><subject>calcium treatment</subject><subject>shape control</subject><subject>steelmaking</subject><issn>0021-1575</issn><issn>1883-2954</issn><fulltext>true</fulltext><rsrctype>article</rsrctype><creationdate>2007</creationdate><recordtype>article</recordtype><recordid>eNplkMtOwzAQRS0EEhX0D1hkxS7FjuMkXlbl0UqVWFDW1sSPNsiJi-0s-ve4CiAhNjOaO_dcaQahO4IXBWXsIeoYxugOsIdBLzhdJPECzUjT0LzgrLxEM4wLkhNWs2s0D6Fr01w2tKbFDK3fDnDU2coN0TubOZMt7dh3A2SbQdoxdG4IWXvKHt3Y2uQDK7uxz5ZKdTHtsp3XEHs9xFt0ZcAGPf_uN-j9-Wm3Wufb15fNarnNJeVlzNuiViVIZSpa1LwCQgzWipcYtKkwawwoWZG2NlRBSzAwSqHSDecUiNLA6Q26n3KP3n2OOkTRd0Fqa9P1bgyi4JwTjstkLCej9C4Er404-q4HfxIEi_PnxJ_PCU5FEhO2mbCPEGGvfyHwsZNW_4fYVM6BPx55AC_0QL8AFziCRg</recordid><startdate>20070501</startdate><enddate>20070501</enddate><creator>ITO, Yo-ichi</creator><creator>NARA, Seikoh</creator><creator>KATO, Yoshiei</creator><creator>SUDA, Mamoru</creator><general>The Iron and Steel Institute of Japan</general><scope>AAYXX</scope><scope>CITATION</scope><scope>7QF</scope><scope>8BQ</scope><scope>8FD</scope><scope>JG9</scope></search><sort><creationdate>20070501</creationdate><title>Shape Control of Alumina Inclusions by Double Calcium Addition Treatment</title><author>ITO, Yo-ichi ; NARA, Seikoh ; KATO, Yoshiei ; SUDA, Mamoru</author></sort><facets><frbrtype>5</frbrtype><frbrgroupid>cdi_FETCH-LOGICAL-c394t-b27d4acdf632796a11f0ed940aef6058fadc61b7f3dab10a533a6e8993a1dea93</frbrgroupid><rsrctype>articles</rsrctype><prefilter>articles</prefilter><language>jpn</language><creationdate>2007</creationdate><topic>alumina inclusion</topic><topic>calcium treatment</topic><topic>shape control</topic><topic>steelmaking</topic><toplevel>peer_reviewed</toplevel><toplevel>online_resources</toplevel><creatorcontrib>ITO, Yo-ichi</creatorcontrib><creatorcontrib>NARA, Seikoh</creatorcontrib><creatorcontrib>KATO, Yoshiei</creatorcontrib><creatorcontrib>SUDA, Mamoru</creatorcontrib><collection>CrossRef</collection><collection>Aluminium Industry Abstracts</collection><collection>METADEX</collection><collection>Technology Research Database</collection><collection>Materials Research Database</collection><jtitle>Tetsu to hagane</jtitle></facets><delivery><delcategory>Remote Search Resource</delcategory><fulltext>fulltext</fulltext></delivery><addata><au>ITO, Yo-ichi</au><au>NARA, Seikoh</au><au>KATO, Yoshiei</au><au>SUDA, Mamoru</au><format>journal</format><genre>article</genre><ristype>JOUR</ristype><atitle>Shape Control of Alumina Inclusions by Double Calcium Addition Treatment</atitle><jtitle>Tetsu to hagane</jtitle><addtitle>Tetsu-to-Hagane</addtitle><date>2007-05-01</date><risdate>2007</risdate><volume>93</volume><issue>5</issue><spage>355</spage><epage>361</epage><pages>355-361</pages><issn>0021-1575</issn><eissn>1883-2954</eissn><abstract>Experimental and theoretical studies were carried out to clarify shape control of alumina inclusions during calcium double treatment in a line pipe steel for sour service. Calcium (Ca) double addition method were experimented by 280 t-scale commercial plant. In this method, Ca powder was firstly injected for shape control of alumina inclusions by flux injection process (FI), and was secondly added for shape control of MnS to CaS in tundish of continuous casting machine after eliminating the first step Ca by RH degasser. The degree of shape control of alumina inclusions of this method was increased compared with that of the conventional Ca treatment by FI or tundish addition, and approaches to the equilibrium condition among Ca-CaO-Al2O3 system. To explain the shape control rate of alumina inclusions, the non-reacted core model fitted by the laboratory scale experimental results was applied for this experimental data. The calculated values from this model in the Ca double addition method agreed well with the observed ones.</abstract><pub>The Iron and Steel Institute of Japan</pub><doi>10.2355/tetsutohagane.93.355</doi><tpages>7</tpages><oa>free_for_read</oa></addata></record> |
| fulltext | fulltext |
| identifier | ISSN: 0021-1575 |
| ispartof | Tetsu-to-Hagane, 2007/05/01, Vol.93(5), pp.355-361 |
| issn | 0021-1575 1883-2954 |
| language | jpn |
| recordid | cdi_proquest_miscellaneous_29991904 |
| source | EZB Electronic Journals Library; J-STAGE |
| subjects | alumina inclusion calcium treatment shape control steelmaking |
| title | Shape Control of Alumina Inclusions by Double Calcium Addition Treatment |
| url | https://sfx.bib-bvb.de/sfx_tum?ctx_ver=Z39.88-2004&ctx_enc=info:ofi/enc:UTF-8&ctx_tim=2025-01-01T10%3A59%3A59IST&url_ver=Z39.88-2004&url_ctx_fmt=infofi/fmt:kev:mtx:ctx&rfr_id=info:sid/primo.exlibrisgroup.com:primo3-Article-proquest_cross&rft_val_fmt=info:ofi/fmt:kev:mtx:journal&rft.genre=article&rft.atitle=Shape%20Control%20of%20Alumina%20Inclusions%20by%20Double%20Calcium%20Addition%20Treatment&rft.jtitle=Tetsu%20to%20hagane&rft.au=ITO,%20Yo-ichi&rft.date=2007-05-01&rft.volume=93&rft.issue=5&rft.spage=355&rft.epage=361&rft.pages=355-361&rft.issn=0021-1575&rft.eissn=1883-2954&rft_id=info:doi/10.2355/tetsutohagane.93.355&rft_dat=%3Cproquest_cross%3E29991904%3C/proquest_cross%3E%3Curl%3E%3C/url%3E&disable_directlink=true&sfx.directlink=off&sfx.report_link=0&rft_id=info:oai/&rft_pqid=29991904&rft_id=info:pmid/&rfr_iscdi=true |