Prior corrosion and fatigue of 2024-T3 aluminum alloy

Pit-to-crack transition experiments were conducted on two thicknesses of 2024-T3 aluminum alloy. Specimens were corroded using a 15:1 ratio of 3.5% sodium chloride solution and hydrogen peroxide prior to fatigue loading. Cracks originating from corrosion pits were visually investigated using various...