Fatigue damage in bulk metallic glass II: Experiments

Cyclic fatigue was investigated in metallic glasses using fracture mechanics-based crack-growth and stress-life experiments. Steady-state crack growth in a Zr-based bulk metallic glass occurred with a Paris law exponent of ∼1.5. Growing planar fatigue cracks were often noted to destabilize into a wa...