Welding of Aluminum and Steel by Friction Stir Diffusion Process

Welding of Aluminum and Steel by Friction Stir Diffusion Process

Welding between ADC12 and SS400 was successfully performed by friction stir diffusion process. The experiments were conducted by a machining center with a cemented carbide tool and welding conditions, such as a rotating speed, welding speed and position of the tool, were optimized. By plunging the r...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Materials science forum 2004-03, Vol.449-452, p.433-436
Hauptverfasser: Fukumoto, Masahiro, Tsubaki, Masami, Shimoda, Youichirou, Yasui, Toshiaki
Format: Artikel
Sprache:eng
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
container_end_page 436
container_issue
container_start_page 433
container_title Materials science forum
container_volume 449-452
creator Fukumoto, Masahiro
Tsubaki, Masami
Shimoda, Youichirou
Yasui, Toshiaki
description Welding between ADC12 and SS400 was successfully performed by friction stir diffusion process. The experiments were conducted by a machining center with a cemented carbide tool and welding conditions, such as a rotating speed, welding speed and position of the tool, were optimized. By plunging the rotating tool into the interface with offset, ADC12 and SS400 were welded above 2000 rpm of the rotating speed at the welding speed of 50mm/min. Tensile strength was evaluated for the welded specimens. The specimens fabricated above 5000rpm in the rotating speed were fractured at the weld zone and showed relatively low tensile strength. The specimens, on the other hand, made between 2000 and 4000 rpm were fractured in the portion of the base aluminum alloy. Achievement of more than 100% in joint efficiency was indicated in the present friction stirring process.
doi_str_mv 10.4028/www.scientific.net/MSF.449-452.433
format Article
fullrecord <record><control><sourceid>proquest_cross</sourceid><recordid>TN_cdi_proquest_miscellaneous_28488855</recordid><sourceformat>XML</sourceformat><sourcesystem>PC</sourcesystem><sourcerecordid>28488855</sourcerecordid><originalsourceid>FETCH-LOGICAL-c3503-e597857182f27df7457e18758a10afb82fbf1b1357e994e27a5018307fc719273</originalsourceid><addsrcrecordid>eNqV0F1LwzAUBuAgCs7pf-iVF0K7fDbpnXNzKkwUpngZ0izRjDadScvYvzdjgtdeHc7L4YXzAHCDYEEhFpPdbldE7YzvnXW68KafPK8WBaVVThkuKCEnYITKEucVZ_gUjCBmLGeUl-fgIsYNhAQJVI7A7Ydp1s5_Zp3Nps3QOj-0mfLrbNUb02T1PlsEp3vX-ZS4kM2dtUM8rK-h0ybGS3BmVRPN1e8cg_fF_dvsMV--PDzNpstcEwZJbljFBeNIYIv52nLKuEGCM6EQVLZOcW1RjUiKq4oazBWDSBDIreaowpyMwfWxdxu678HEXrYuatM0yptuiBILKoRgLB3eHQ916GIMxsptcK0Ke4mgPODJhCf_8GTCkwlPJjyZ8GTCSyXzY0kflI-90V9y0w3Bpw__U_MDEYSBEQ</addsrcrecordid><sourcetype>Aggregation Database</sourcetype><iscdi>true</iscdi><recordtype>article</recordtype><pqid>28488855</pqid></control><display><type>article</type><title>Welding of Aluminum and Steel by Friction Stir Diffusion Process</title><source>Scientific.net Journals</source><creator>Fukumoto, Masahiro ; Tsubaki, Masami ; Shimoda, Youichirou ; Yasui, Toshiaki</creator><creatorcontrib>Fukumoto, Masahiro ; Tsubaki, Masami ; Shimoda, Youichirou ; Yasui, Toshiaki</creatorcontrib><description>Welding between ADC12 and SS400 was successfully performed by friction stir diffusion process. The experiments were conducted by a machining center with a cemented carbide tool and welding conditions, such as a rotating speed, welding speed and position of the tool, were optimized. By plunging the rotating tool into the interface with offset, ADC12 and SS400 were welded above 2000 rpm of the rotating speed at the welding speed of 50mm/min. Tensile strength was evaluated for the welded specimens. The specimens fabricated above 5000rpm in the rotating speed were fractured at the weld zone and showed relatively low tensile strength. The specimens, on the other hand, made between 2000 and 4000 rpm were fractured in the portion of the base aluminum alloy. Achievement of more than 100% in joint efficiency was indicated in the present friction stirring process.</description><identifier>ISSN: 0255-5476</identifier><identifier>ISSN: 1662-9752</identifier><identifier>EISSN: 1662-9752</identifier><identifier>DOI: 10.4028/www.scientific.net/MSF.449-452.433</identifier><language>eng</language><publisher>Trans Tech Publications Ltd</publisher><ispartof>Materials science forum, 2004-03, Vol.449-452, p.433-436</ispartof><rights>2004 Trans Tech Publications Ltd</rights><lds50>peer_reviewed</lds50><woscitedreferencessubscribed>false</woscitedreferencessubscribed><citedby>FETCH-LOGICAL-c3503-e597857182f27df7457e18758a10afb82fbf1b1357e994e27a5018307fc719273</citedby><cites>FETCH-LOGICAL-c3503-e597857182f27df7457e18758a10afb82fbf1b1357e994e27a5018307fc719273</cites></display><links><openurl>$$Topenurl_article</openurl><openurlfulltext>$$Topenurlfull_article</openurlfulltext><thumbnail>$$Uhttps://www.scientific.net/Image/TitleCover/489?width=600</thumbnail><link.rule.ids>314,776,780,27903,27904</link.rule.ids></links><search><creatorcontrib>Fukumoto, Masahiro</creatorcontrib><creatorcontrib>Tsubaki, Masami</creatorcontrib><creatorcontrib>Shimoda, Youichirou</creatorcontrib><creatorcontrib>Yasui, Toshiaki</creatorcontrib><title>Welding of Aluminum and Steel by Friction Stir Diffusion Process</title><title>Materials science forum</title><description>Welding between ADC12 and SS400 was successfully performed by friction stir diffusion process. The experiments were conducted by a machining center with a cemented carbide tool and welding conditions, such as a rotating speed, welding speed and position of the tool, were optimized. By plunging the rotating tool into the interface with offset, ADC12 and SS400 were welded above 2000 rpm of the rotating speed at the welding speed of 50mm/min. Tensile strength was evaluated for the welded specimens. The specimens fabricated above 5000rpm in the rotating speed were fractured at the weld zone and showed relatively low tensile strength. The specimens, on the other hand, made between 2000 and 4000 rpm were fractured in the portion of the base aluminum alloy. Achievement of more than 100% in joint efficiency was indicated in the present friction stirring process.</description><issn>0255-5476</issn><issn>1662-9752</issn><issn>1662-9752</issn><fulltext>true</fulltext><rsrctype>article</rsrctype><creationdate>2004</creationdate><recordtype>article</recordtype><recordid>eNqV0F1LwzAUBuAgCs7pf-iVF0K7fDbpnXNzKkwUpngZ0izRjDadScvYvzdjgtdeHc7L4YXzAHCDYEEhFpPdbldE7YzvnXW68KafPK8WBaVVThkuKCEnYITKEucVZ_gUjCBmLGeUl-fgIsYNhAQJVI7A7Ydp1s5_Zp3Nps3QOj-0mfLrbNUb02T1PlsEp3vX-ZS4kM2dtUM8rK-h0ybGS3BmVRPN1e8cg_fF_dvsMV--PDzNpstcEwZJbljFBeNIYIv52nLKuEGCM6EQVLZOcW1RjUiKq4oazBWDSBDIreaowpyMwfWxdxu678HEXrYuatM0yptuiBILKoRgLB3eHQ916GIMxsptcK0Ke4mgPODJhCf_8GTCkwlPJjyZ8GTCSyXzY0kflI-90V9y0w3Bpw__U_MDEYSBEQ</recordid><startdate>20040315</startdate><enddate>20040315</enddate><creator>Fukumoto, Masahiro</creator><creator>Tsubaki, Masami</creator><creator>Shimoda, Youichirou</creator><creator>Yasui, Toshiaki</creator><general>Trans Tech Publications Ltd</general><scope>AAYXX</scope><scope>CITATION</scope><scope>7QF</scope><scope>8BQ</scope><scope>8FD</scope><scope>JG9</scope></search><sort><creationdate>20040315</creationdate><title>Welding of Aluminum and Steel by Friction Stir Diffusion Process</title><author>Fukumoto, Masahiro ; Tsubaki, Masami ; Shimoda, Youichirou ; Yasui, Toshiaki</author></sort><facets><frbrtype>5</frbrtype><frbrgroupid>cdi_FETCH-LOGICAL-c3503-e597857182f27df7457e18758a10afb82fbf1b1357e994e27a5018307fc719273</frbrgroupid><rsrctype>articles</rsrctype><prefilter>articles</prefilter><language>eng</language><creationdate>2004</creationdate><toplevel>peer_reviewed</toplevel><toplevel>online_resources</toplevel><creatorcontrib>Fukumoto, Masahiro</creatorcontrib><creatorcontrib>Tsubaki, Masami</creatorcontrib><creatorcontrib>Shimoda, Youichirou</creatorcontrib><creatorcontrib>Yasui, Toshiaki</creatorcontrib><collection>CrossRef</collection><collection>Aluminium Industry Abstracts</collection><collection>METADEX</collection><collection>Technology Research Database</collection><collection>Materials Research Database</collection><jtitle>Materials science forum</jtitle></facets><delivery><delcategory>Remote Search Resource</delcategory><fulltext>fulltext</fulltext></delivery><addata><au>Fukumoto, Masahiro</au><au>Tsubaki, Masami</au><au>Shimoda, Youichirou</au><au>Yasui, Toshiaki</au><format>journal</format><genre>article</genre><ristype>JOUR</ristype><atitle>Welding of Aluminum and Steel by Friction Stir Diffusion Process</atitle><jtitle>Materials science forum</jtitle><date>2004-03-15</date><risdate>2004</risdate><volume>449-452</volume><spage>433</spage><epage>436</epage><pages>433-436</pages><issn>0255-5476</issn><issn>1662-9752</issn><eissn>1662-9752</eissn><abstract>Welding between ADC12 and SS400 was successfully performed by friction stir diffusion process. The experiments were conducted by a machining center with a cemented carbide tool and welding conditions, such as a rotating speed, welding speed and position of the tool, were optimized. By plunging the rotating tool into the interface with offset, ADC12 and SS400 were welded above 2000 rpm of the rotating speed at the welding speed of 50mm/min. Tensile strength was evaluated for the welded specimens. The specimens fabricated above 5000rpm in the rotating speed were fractured at the weld zone and showed relatively low tensile strength. The specimens, on the other hand, made between 2000 and 4000 rpm were fractured in the portion of the base aluminum alloy. Achievement of more than 100% in joint efficiency was indicated in the present friction stirring process.</abstract><pub>Trans Tech Publications Ltd</pub><doi>10.4028/www.scientific.net/MSF.449-452.433</doi><tpages>4</tpages></addata></record>
fulltext fulltext
identifier ISSN: 0255-5476
ispartof Materials science forum, 2004-03, Vol.449-452, p.433-436
issn 0255-5476
1662-9752
1662-9752
language eng
recordid cdi_proquest_miscellaneous_28488855
source Scientific.net Journals
title Welding of Aluminum and Steel by Friction Stir Diffusion Process
url https://sfx.bib-bvb.de/sfx_tum?ctx_ver=Z39.88-2004&ctx_enc=info:ofi/enc:UTF-8&ctx_tim=2025-01-25T16%3A50%3A50IST&url_ver=Z39.88-2004&url_ctx_fmt=infofi/fmt:kev:mtx:ctx&rfr_id=info:sid/primo.exlibrisgroup.com:primo3-Article-proquest_cross&rft_val_fmt=info:ofi/fmt:kev:mtx:journal&rft.genre=article&rft.atitle=Welding%20of%20Aluminum%20and%20Steel%20by%20Friction%20Stir%20Diffusion%20Process&rft.jtitle=Materials%20science%20forum&rft.au=Fukumoto,%20Masahiro&rft.date=2004-03-15&rft.volume=449-452&rft.spage=433&rft.epage=436&rft.pages=433-436&rft.issn=0255-5476&rft.eissn=1662-9752&rft_id=info:doi/10.4028/www.scientific.net/MSF.449-452.433&rft_dat=%3Cproquest_cross%3E28488855%3C/proquest_cross%3E%3Curl%3E%3C/url%3E&disable_directlink=true&sfx.directlink=off&sfx.report_link=0&rft_id=info:oai/&rft_pqid=28488855&rft_id=info:pmid/&rfr_iscdi=true