Fracture strength of melt-infiltrated SiC-mullite composite

The fracture strength of a melt-infiltrated SiC-mullite composite was measured from room temperature to 1500°C using a three-point bending test. The strength under argon at atmospheric pressure was not high. Mullite decomposition was found to be severe even at 1100°C in a reducing atmosphere, thus s...

Ausführliche Beschreibung

Gespeichert in:

Bibliographische Detailangaben
Veröffentlicht in:	Journal of materials science 2004-06, Vol.39 (11), p.3751-3755
Hauptverfasser:	Tian, J, Shobu, K
Format:	Artikel
Sprache:	eng
Schlagworte:	air ambient temperature Applied sciences Argon argon (noble gases) atmospheric pressure Bend strength Building materials. Ceramics. Glasses Ceramic industries Cermets, ceramic and refractory composites Chemical industry and chemicals Crack propagation Cross-disciplinary physics: materials science rheology Decomposition Exact sciences and technology Fracture strength High temperature Materials science Mullite Other materials Physics Specific materials Structural ceramics Technical ceramics
Online-Zugang:	Volltext
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!

Schreiben Sie den ersten Kommentar!