Effect of Stress Ratio on Long Life Fatigue Behavior of High Carbon Chromium Bearing Steel under Axial Loading

Effect of Stress Ratio on Long Life Fatigue Behavior of High Carbon Chromium Bearing Steel under Axial Loading

The effect of stress ratio in fatigue properties of bearing steel including long life region was experimentally examined under axial loading. As a result, the complicated S-N property was, irrespective of stress ratio, well explained as duplex S-N characteristics obtained by superposition of S-N cur...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Nihon Kikai Gakkai ronbunshū. A 2004-06, Vol.16 (6), p.850-857
Hauptverfasser: Sakai, Tatsuo, Sato, Yosuke, Nagano, Yoshiyuki, Takeda, Mitsuhiro, Oguma, Noriyasu
Format: Artikel
Sprache:jpn
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
container_end_page 857
container_issue 6
container_start_page 850
container_title Nihon Kikai Gakkai ronbunshū. A
container_volume 16
creator Sakai, Tatsuo
Sato, Yosuke
Nagano, Yoshiyuki
Takeda, Mitsuhiro
Oguma, Noriyasu
description The effect of stress ratio in fatigue properties of bearing steel including long life region was experimentally examined under axial loading. As a result, the complicated S-N property was, irrespective of stress ratio, well explained as duplex S-N characteristics obtained by superposition of S-N curves for surface induced fracture and interior inclusion induced fracture. Fish-eye marks were necessarily observed on the fracture surfaces failed in the latter fracture mode and an inclusion was found at the center of the fish-eye. It was finally found that the fatigue fracture of this steel in the long life region occurred through three different processes of ( 1) formation of the characteristic area of FGA, ( 2) crack propagation to form the fish-eye and ( 3) rapid crack propagation to cause the catastrophic fracture.
format Article
fullrecord <record><control><sourceid>proquest</sourceid><recordid>TN_cdi_proquest_miscellaneous_28166982</recordid><sourceformat>XML</sourceformat><sourcesystem>PC</sourcesystem><sourcerecordid>28166982</sourcerecordid><originalsourceid>FETCH-proquest_miscellaneous_281669823</originalsourceid><addsrcrecordid>eNqNzE0KwjAQBeAsFBTtHWblTkhbrHWppcWFK3UvaZ20A2mi-RGPbwQP4Grgve_NhM15Xm7XG87LGUuco5bzPN2mvMjmTNdSYufBSLh4i87BWXgyYDScjO7hRBKhiVEfEA44iBcZ-9VH6geohG2jrAZrRgpjBMJSXF08ooKg72hh_yah4jNxj82STaVQDpPfXbBVU1-r4_phzTOg87eRXIdKCY0muFtWpkWxK7P8b_gBPyhL3Q</addsrcrecordid><sourcetype>Aggregation Database</sourcetype><iscdi>true</iscdi><recordtype>article</recordtype><pqid>28166982</pqid></control><display><type>article</type><title>Effect of Stress Ratio on Long Life Fatigue Behavior of High Carbon Chromium Bearing Steel under Axial Loading</title><source>J-STAGE (Japan Science &amp; Technology Information Aggregator, Electronic) Freely Available Titles - Japanese</source><source>Elektronische Zeitschriftenbibliothek - Frei zugängliche E-Journals</source><creator>Sakai, Tatsuo ; Sato, Yosuke ; Nagano, Yoshiyuki ; Takeda, Mitsuhiro ; Oguma, Noriyasu</creator><creatorcontrib>Sakai, Tatsuo ; Sato, Yosuke ; Nagano, Yoshiyuki ; Takeda, Mitsuhiro ; Oguma, Noriyasu</creatorcontrib><description>The effect of stress ratio in fatigue properties of bearing steel including long life region was experimentally examined under axial loading. As a result, the complicated S-N property was, irrespective of stress ratio, well explained as duplex S-N characteristics obtained by superposition of S-N curves for surface induced fracture and interior inclusion induced fracture. Fish-eye marks were necessarily observed on the fracture surfaces failed in the latter fracture mode and an inclusion was found at the center of the fish-eye. It was finally found that the fatigue fracture of this steel in the long life region occurred through three different processes of ( 1) formation of the characteristic area of FGA, ( 2) crack propagation to form the fish-eye and ( 3) rapid crack propagation to cause the catastrophic fracture.</description><identifier>ISSN: 0387-5008</identifier><language>jpn</language><ispartof>Nihon Kikai Gakkai ronbunshū. A, 2004-06, Vol.16 (6), p.850-857</ispartof><woscitedreferencessubscribed>false</woscitedreferencessubscribed></display><links><openurl>$$Topenurl_article</openurl><openurlfulltext>$$Topenurlfull_article</openurlfulltext><thumbnail>$$Tsyndetics_thumb_exl</thumbnail><link.rule.ids>314,776,780</link.rule.ids></links><search><creatorcontrib>Sakai, Tatsuo</creatorcontrib><creatorcontrib>Sato, Yosuke</creatorcontrib><creatorcontrib>Nagano, Yoshiyuki</creatorcontrib><creatorcontrib>Takeda, Mitsuhiro</creatorcontrib><creatorcontrib>Oguma, Noriyasu</creatorcontrib><title>Effect of Stress Ratio on Long Life Fatigue Behavior of High Carbon Chromium Bearing Steel under Axial Loading</title><title>Nihon Kikai Gakkai ronbunshū. A</title><description>The effect of stress ratio in fatigue properties of bearing steel including long life region was experimentally examined under axial loading. As a result, the complicated S-N property was, irrespective of stress ratio, well explained as duplex S-N characteristics obtained by superposition of S-N curves for surface induced fracture and interior inclusion induced fracture. Fish-eye marks were necessarily observed on the fracture surfaces failed in the latter fracture mode and an inclusion was found at the center of the fish-eye. It was finally found that the fatigue fracture of this steel in the long life region occurred through three different processes of ( 1) formation of the characteristic area of FGA, ( 2) crack propagation to form the fish-eye and ( 3) rapid crack propagation to cause the catastrophic fracture.</description><issn>0387-5008</issn><fulltext>true</fulltext><rsrctype>article</rsrctype><creationdate>2004</creationdate><recordtype>article</recordtype><recordid>eNqNzE0KwjAQBeAsFBTtHWblTkhbrHWppcWFK3UvaZ20A2mi-RGPbwQP4Grgve_NhM15Xm7XG87LGUuco5bzPN2mvMjmTNdSYufBSLh4i87BWXgyYDScjO7hRBKhiVEfEA44iBcZ-9VH6geohG2jrAZrRgpjBMJSXF08ooKg72hh_yah4jNxj82STaVQDpPfXbBVU1-r4_phzTOg87eRXIdKCY0muFtWpkWxK7P8b_gBPyhL3Q</recordid><startdate>20040601</startdate><enddate>20040601</enddate><creator>Sakai, Tatsuo</creator><creator>Sato, Yosuke</creator><creator>Nagano, Yoshiyuki</creator><creator>Takeda, Mitsuhiro</creator><creator>Oguma, Noriyasu</creator><scope>7TB</scope><scope>8BQ</scope><scope>8FD</scope><scope>FR3</scope><scope>JG9</scope><scope>KR7</scope></search><sort><creationdate>20040601</creationdate><title>Effect of Stress Ratio on Long Life Fatigue Behavior of High Carbon Chromium Bearing Steel under Axial Loading</title><author>Sakai, Tatsuo ; Sato, Yosuke ; Nagano, Yoshiyuki ; Takeda, Mitsuhiro ; Oguma, Noriyasu</author></sort><facets><frbrtype>5</frbrtype><frbrgroupid>cdi_FETCH-proquest_miscellaneous_281669823</frbrgroupid><rsrctype>articles</rsrctype><prefilter>articles</prefilter><language>jpn</language><creationdate>2004</creationdate><toplevel>online_resources</toplevel><creatorcontrib>Sakai, Tatsuo</creatorcontrib><creatorcontrib>Sato, Yosuke</creatorcontrib><creatorcontrib>Nagano, Yoshiyuki</creatorcontrib><creatorcontrib>Takeda, Mitsuhiro</creatorcontrib><creatorcontrib>Oguma, Noriyasu</creatorcontrib><collection>Mechanical &amp; Transportation Engineering Abstracts</collection><collection>METADEX</collection><collection>Technology Research Database</collection><collection>Engineering Research Database</collection><collection>Materials Research Database</collection><collection>Civil Engineering Abstracts</collection><jtitle>Nihon Kikai Gakkai ronbunshū. A</jtitle></facets><delivery><delcategory>Remote Search Resource</delcategory><fulltext>fulltext</fulltext></delivery><addata><au>Sakai, Tatsuo</au><au>Sato, Yosuke</au><au>Nagano, Yoshiyuki</au><au>Takeda, Mitsuhiro</au><au>Oguma, Noriyasu</au><format>journal</format><genre>article</genre><ristype>JOUR</ristype><atitle>Effect of Stress Ratio on Long Life Fatigue Behavior of High Carbon Chromium Bearing Steel under Axial Loading</atitle><jtitle>Nihon Kikai Gakkai ronbunshū. A</jtitle><date>2004-06-01</date><risdate>2004</risdate><volume>16</volume><issue>6</issue><spage>850</spage><epage>857</epage><pages>850-857</pages><issn>0387-5008</issn><abstract>The effect of stress ratio in fatigue properties of bearing steel including long life region was experimentally examined under axial loading. As a result, the complicated S-N property was, irrespective of stress ratio, well explained as duplex S-N characteristics obtained by superposition of S-N curves for surface induced fracture and interior inclusion induced fracture. Fish-eye marks were necessarily observed on the fracture surfaces failed in the latter fracture mode and an inclusion was found at the center of the fish-eye. It was finally found that the fatigue fracture of this steel in the long life region occurred through three different processes of ( 1) formation of the characteristic area of FGA, ( 2) crack propagation to form the fish-eye and ( 3) rapid crack propagation to cause the catastrophic fracture.</abstract></addata></record>
fulltext fulltext
identifier ISSN: 0387-5008
ispartof Nihon Kikai Gakkai ronbunshū. A, 2004-06, Vol.16 (6), p.850-857
issn 0387-5008
language jpn
recordid cdi_proquest_miscellaneous_28166982
source J-STAGE (Japan Science & Technology Information Aggregator, Electronic) Freely Available Titles - Japanese; Elektronische Zeitschriftenbibliothek - Frei zugängliche E-Journals
title Effect of Stress Ratio on Long Life Fatigue Behavior of High Carbon Chromium Bearing Steel under Axial Loading
url https://sfx.bib-bvb.de/sfx_tum?ctx_ver=Z39.88-2004&ctx_enc=info:ofi/enc:UTF-8&ctx_tim=2025-02-08T05%3A32%3A18IST&url_ver=Z39.88-2004&url_ctx_fmt=infofi/fmt:kev:mtx:ctx&rfr_id=info:sid/primo.exlibrisgroup.com:primo3-Article-proquest&rft_val_fmt=info:ofi/fmt:kev:mtx:journal&rft.genre=article&rft.atitle=Effect%20of%20Stress%20Ratio%20on%20Long%20Life%20Fatigue%20Behavior%20of%20High%20Carbon%20Chromium%20Bearing%20Steel%20under%20Axial%20Loading&rft.jtitle=Nihon%20Kikai%20Gakkai%20ronbunsh%C5%AB.%20A&rft.au=Sakai,%20Tatsuo&rft.date=2004-06-01&rft.volume=16&rft.issue=6&rft.spage=850&rft.epage=857&rft.pages=850-857&rft.issn=0387-5008&rft_id=info:doi/&rft_dat=%3Cproquest%3E28166982%3C/proquest%3E%3Curl%3E%3C/url%3E&disable_directlink=true&sfx.directlink=off&sfx.report_link=0&rft_id=info:oai/&rft_pqid=28166982&rft_id=info:pmid/&rfr_iscdi=true